Fatigue Crack Initiation and Extension Regularity Based on Damage Mechanics

被引：0
|
作者：
Sun Z. [1 ]
Chai X. [1 ]
Liu X. [1 ]
Wang J. [1 ]
机构：
[1] School of Mechanical Engineering & Automation, Northeastern University, Shenyang
来源：
Cailiao Daobao/Materials Review | 2017年 / 31卷 / 04期
关键词：
Crack grown rate; Damage mechanics; Fatigue crack; Fatigue life;
D O I：
10.11896/j.issn.1005-023X.2017.08.026
中图分类号：
学科分类号：
摘要：
Aiming at the problem of metal fatigue crack initiation and propagation life forecast, an unified a model was presented based on damage mechanics and finite element method, and the calculating program was established.The stiffness matrix was continuously calculated by introducing the additional loading method.The calculating program was designed in MATLAB and the calculation flow diagram was showed in this paper.Then through the calculation of a single cell, the changing process of equivalent stress was presented with the cell from undamaged state to completely damaged state and the reasons of the changes were analyzed. It was found that the crack initiation and propagation life was more than 80% of the total life. By finite element software ANSYS simulation, the crack initiation and propagation process of notched specimen were obtained. Finally, the results of theoretical calculation and the experimental data were basically identical, which verify the accuracy of this method. © 2017, Materials Review Magazine. All right reserved.
引用
收藏
页码：130 / 134
页数：4
相关论文
共 12 条
  • [1] Gagg C.R., Lewis P.R., In-service fatigue failure of engineered products and structures-Case study review, Eng Failure Analysis, 16, (2009)
  • [2] Zheng J., Wu L., Shi J., Extreme pressure equipments, Chin J Mech Eng, 24, 2, (2011)
  • [3] Riahi H., Bressolette P.H., Chateauneuf A., Random mode by stochastic collocation method, Eng Fatigue Crack Growth Mixed Fracture Mech, 77, (2010)
  • [4] Li A., Cui H., Wen W., Et al., Prediction of fretting fatigue life based on nonlinear continuum damage mechanics, Acta Aeronautica et Astronautica Sinica, 34, 9, (2013)
  • [5] Li Q., Zhang L., Qi Q., Et al., Study of the curve branch crack model for the closed flaw under compressive loading, Eng Mech, 30, 4, (2013)
  • [6] Shangguan W., Wang X., Duan X., Et al., Fatigue crack growth experiment and modeling for rubbers used in isolators under variable amplitude loads, J Mech Eng, 51, 8, (2015)
  • [7] Yang J., Zhang X., Zhang M., Numerical method for crack extension analysis based on fatigue crack formation curve, J Mech Eng, 40, 7, (2004)
  • [8] Dattoma V., Giancane S., Nobile R., Et al., Fatigue life prediction under variable loading based on a new non-linear continuum damage mechanics model, Int J Fatigue, 28, 89, (2006)
  • [9] Gou Y., Yin Z., Huang Q., A finite element method for prediction of pitting-corrosion fatigue life based on damage mechanics, Adv Aeronautical Sci Eng, 2, 5, (2014)
  • [10] Li Y., Ma Q., Guo X., Et al., Crack initiation life prediction of notch structure based on damage mechanics, J Machine Des, 32, 12, (2015)
12