BI,PB(2212) AND BI(2223) FORMATION IN THE BI-PB-SR-CA-CU-O SYSTEM

被引：69
|
作者：
JEREMIE, A
ALAMIYADRI, K
GRIVEL, JC
FLUKIGER, R
机构：
[1] Dept. de la Matiere Condensee, Geneva Univ.
来源：
SUPERCONDUCTOR SCIENCE & TECHNOLOGY | 1993年 / 6卷 / 10期
关键词：
D O I：
10.1088/0953-2048/6/10/005
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
A new route has been found for producing the Bi2Sr2CaCu2Oy phase with Pb substituted for part of the Bi (denoted Bi,Pb(2212)). By this novel route, Bi,Pb(2212) has been prepared in air at 860-degrees-C. For comparison, this phase has also been prepared in argon at 740-degrees-C by the previously known route. Bi,Pb(2212) transforms from a tetragonal to an orthorhombic structure as the Pb content grows. Once this phase was obtained with a nominal composition of Bi2-xPbxSr2CaCu2Oy with Pb contents x = 0, 0.2, 0.4 and 0.6, the Bi(2223) phase was formed starting from Bi(2212) and Bi,Pb(2212). Single-phase samples were obtained after two heat treatments at 849-degrees-C with Bi,Pb(2212) and a proportion of Pb of x = 0.4. This proportion corresponds to the one used previously by the authors to obtain high critical current carrying tapes in Ag-clad Bi(2223) tapes.
引用
收藏
页码：730 / 735
页数：6
相关论文
共 50 条
  • [21] SUPERCONDUCTIVITY IN THE BI-PB-SR-CA-CU-O SYSTEM WITH OXIDE ADDITIONS
    DOU, SX
    LIU, HK
    GUO, SJ
    EASTERLING, KE
    MIKAEL, J
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1989, 2 (05): : 274 - 278
  • [22] STACKING POLYTYPES IN THE SYSTEMS BI-PB-SR-CA-MN-O, BI-PB-SR-CA-FE-O, BI-PB-SR-CA-CO-O, BI-PB-SR-CA-NI-O, BI-PB-SR-CA-CU-O WITH T = MN, FE, CO, NI, CU
    EHMANN, A
    FRIES, T
    KEMMLERSACK, S
    LOSCH, S
    RENTSCHLER, T
    RYGULA, M
    SCHLICHENMAIER, M
    WISCHERT, W
    JOURNAL OF THE LESS-COMMON METALS, 1990, 164 (1-2): : 596 - 603
  • [23] SUPERCONDUCTIVITY IN AG ADDED BI-PB-SR-CA-CU-O SYSTEM
    MUKHERJEE, PS
    SIMON, A
    KOSHY, J
    GURUSWAMY, P
    DAMODARAN, AD
    SOLID STATE COMMUNICATIONS, 1990, 76 (05) : 659 - 661
  • [24] EFFECT OF ANNEALING ON SUPERCONDUCTIVITY IN BI-PB-SR-CA-CU-O SYSTEM
    MATSUDA, M
    KIKUCHI, A
    TAKATA, M
    ISHII, M
    YAMASHITA, T
    KOINUMA, H
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1989, 28 (06): : L940 - L942
  • [25] Rapid formation of high Tc phase in Bi-Pb-Sr-Ca-Cu-O system
    Mancic, L
    Milosevic, O
    Marinkovic, B
    Lopez, MDD
    Rizzo, F
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2000, 341 : 503 - 504
  • [26] CU VALENCE STATES IN SUPERCONDUCTING BI-PB-SR-CA-CU-O SYSTEM
    LIU, HK
    DOU, SX
    SONG, KH
    SORRELL, CC
    EASTERLING, KE
    JONES, WK
    JOURNAL OF SOLID STATE CHEMISTRY, 1990, 87 (02) : 289 - 297
  • [27] Single crystals of 2223 phase in the Bi-Pb-Sr-Ca-Cu-O system: Characterization and Knoop microhardness
    Osipov, VN
    Derkachenko, LI
    Nosov, YG
    Gurin, VN
    Jung, W
    Muller, R
    SOLID STATE COMMUNICATIONS, 1996, 97 (05) : 377 - 380
  • [28] EFFECTS OF SB-INCORPORATION ON THE 2223 PHASE IN THE SUPERCONDUCTING BI-PB-SR-CA-CU-O SYSTEM
    KIM, SH
    LEE, DH
    PARK, JS
    CHO, SK
    LEE, SH
    KIM, KH
    BULLETIN OF THE KOREAN CHEMICAL SOCIETY, 1994, 15 (02) : 115 - 118
  • [29] OXYGEN NONSTOICHIOMETRY OF 2223-PHASE BI-PB-SR-CA-CU-O SYSTEM SUPERCONDUCTING OXIDE
    IDEMOTO, Y
    ICHIKAWA, S
    FUEKI, K
    PHYSICA C, 1991, 181 (1-3): : 171 - 178
  • [30] POSSIBILITIES FOR FORMATION OF THE 110-K PHASE 2223 IN SB OR V DOPED BI-SR-CA-CU-O AND BI-PB-SR-CA-CU-O MATERIALS
    KONSTANTINOV, K
    KOVACHEVA, D
    BALCHEV, N
    KOVACHEV, V
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 1992, 3 (02) : 127 - 131
12345