ELECTROCHEMICAL TESTING METHOD FOR STRESS-CORROSION CRACKING BY SEPARATING CRACK ANODE FROM CATHODE

被引：8

作者：

SUZUKI, T ^{[1
]}

YAMABE, M ^{[1
]}

KITAMURA, Y ^{[1
]}

机构：

[1] AJINOMOTO CO INC,CENT RES LABS,KAWASAKI,JAPAN

来源：

关键词：

D O I：

10.5006/0010-9312-29.2.70

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

引用

页码：70 / 74

页数：5

共 50 条

[41] TRANSGRANULAR STRESS-CORROSION CRACKING
SIERADZKI, K
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1987, 134 (8B) : C425 - C425
[42] Coalescence conditions for stress-corrosion cracking based on interacting crack pairs
Leis, BN
Mohan, R
PROCEEDINGS OF THE SEVENTH (1997) INTERNATIONAL OFFSHORE AND POLAR ENGINEERING CONFERENCE, VOL IV, 1997, 1997, : 607 - 613
[43] METHOD FOR CRACK CONTROL DURING STUDY OF EFFICIENCY OF METAL PROTECTION AGAINST STRESS-CORROSION CRACKING
LAGUTINA, AG
LOGACHEV, VN
YAKUSAR, AI
ZAVODSKAYA LABORATORIYA, 1975, 41 (02): : 224 - 228
[44] CRACK TIP DEFORMATION AND STRESS-CORROSION CRACKING IN 70/30 BRASS
MACKAY, F
EVANS, JT
PARKINS, RN
CORROSION SCIENCE, 1992, 33 (05) : 699 - &
[45] Stress-corrosion cracking in pipelines
Leis, BN
Bubenik, TA
Nestleroth, JB
PIPELINE & GAS JOURNAL, 1996, 223 (08) : 42 - &
[46] Tests for stress-corrosion cracking
Koch, G.H.
Advanced Materials and Processes, 2001, 159 (08): : 36 - 38
[47] STRESS-CORROSION CRACKING OF COPPER
PUGH, EN
MONTAGUE, WG
WESTWOOD, AR
CORROSION SCIENCE, 1966, 6 (07) : 345 - &
[48] STOP STRESS-CORROSION CRACKING
GOSSETT, JL
CHEMICAL ENGINEERING, 1982, 89 (23) : 143 - &
[49] CAUSES OF STRESS-CORROSION CRACKING
BOYD, WK
BATTELLE TECHNICAL REVIEW, 1966, 15 (11): : 5 - &
[50] SUBCRITICAL CRACK-GROWTH - FATIGUE, CREEP AND STRESS-CORROSION CRACKING
TOMKINS, B
PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES, 1981, 299 (1446): : 31 - 44