PLATINUM ALUMINIDE COATING STRUCTURAL EFFECTS ON HOT CORROSION-RESISTANCE AT 900-DEGREES-C

被引：27
|
作者：
DEB, P
BOONE, DH
STREIFF, R
机构：
来源：
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS | 1985年 / 3卷 / 06期
关键词：
D O I：
10.1116/1.572837
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
引用
收藏
页码：2578 / 2581
页数：4
相关论文
共 50 条
  • [41] Improved hot corrosion resistance of TiBw/TA15 composite via pack cementation aluminide coating
    Kang, Qingxin
    Xu, Xiaoting
    Wang, Guofeng
    Chen, Yuqing
    Luo, Shuyi
    CORROSION SCIENCE, 2022, 208
  • [42] ROLE OF PLATINUM IN THE NA2SO4-INDUCED HOT CORROSION-RESISTANCE OF ALUMINUM DIFFUSION COATINGS
    WU, WT
    RAHMEL, A
    SCHORR, M
    OXIDATION OF METALS, 1984, 22 (1-2): : 59 - 81
  • [43] Hot Corrosion Behavior of a Novel Co-base Superalloy in Molten NaCl at 900 degrees C
    Zhang Ying
    Gao Bo
    Wang Lei
    Song Xiu
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2018, 46 (08): : 134 - 139
  • [44] EFFECT OF COATING STRUCTURE ON CORROSION-RESISTANCE OF HOT-DIPPED ZN-AL ALLOY COATED STEEL
    SHIMADA, S
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 : 1229 - 1229
  • [45] EFFECT OF COATING STRUCTURE ON CORROSION-RESISTANCE OF HOT-DIPPED ZN-AL ALLOY COATED STEEL
    SHIMADA, S
    ADANIYA, T
    HARA, T
    ARAKAWA, H
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 26 (01) : B23 - B23
  • [46] THE CORROSION BEHAVIOR OF HIGH-TEMPERATURE ALLOYS DURING EXPOSURE FOR TIMES UP TO 10000 H IN PROTOTYPE NUCLEAR PROCESS HELIUM AT 700-DEGREES-C TO 900-DEGREES-C
    BATES, HGA
    NUCLEAR TECHNOLOGY, 1984, 66 (02) : 415 - 428
  • [47] THE PHASE FIELD OF THE CHEVREL PHASE PBMO6S8 AT 900-DEGREES-C AND SOME SUPERCONDUCTING AND STRUCTURAL-PROPERTIES
    YAMASAKI, H
    KIMURA, Y
    MATERIALS RESEARCH BULLETIN, 1986, 21 (02) : 125 - 135
  • [48] PHASE-STABILITY, OXIDATION, AND INTERDIFFUSION OF A NOVEL NI-CR-AL-TI-SI BOND-COATING ALLOY BETWEEN 900-DEGREES-C AND 1100-DEGREES-C
    LEYENS, C
    FRITSCHER, K
    PETERS, M
    KAYSSER, WA
    OXIDATION OF METALS, 1995, 43 (3-4): : 329 - 352
  • [49] A Zr-doped single-phase Pt-modified aluminide coating and the enhanced hot corrosion resistance
    Jiang, C. Y.
    Yang, Y. F.
    Zhang, Z. Y.
    Bao, Z. B.
    Chen, M. H.
    Zhu, S. L.
    Wang, F. H.
    CORROSION SCIENCE, 2018, 133 : 406 - 416
  • [50] Hot Corrosion Resistance of Sputtered Ni32Co23Cr8Al2Si Nanocrystalline Coating at 900 °C
    Chen Hongyu
    Zhou Yuebo
    Sun Jianfeng
    Zhang Haijun
    RARE METAL MATERIALS AND ENGINEERING, 2013, 42 : 537 - 540
12345