MEASUREMENT OF THE EQUIBIAXIAL ELONGATIONAL VISCOSITY OF POLYSTYRENE USING LUBRICATED SQUEEZING

The equibiaxial elongational viscosity of polystyrene was determined using a lubricated squeezing technique. Constant strain rates up to Hencky strains of 4.5 could be maintained by a newly constructed instrument. Test results from controlled stress and controlled strain rate measurement were consistent and yielded well-defined steady-state viscosities. Measurements appeared to be unaffected by sample geometry, although proper lubrication is important in achieving steady state. The measured biaxial viscosity appeared to be strain rate thinning above a biaxial strain rate of almost-equal-to 0.01 s-1 at 160-degrees-C. As anticipated in the Newtonian region, biaxial elongational viscosity was approximately six times the shear viscosity. Thinning indices of both shear and biaxial elongational viscosities were 0.75. Data obtained at various temperatures were shifted following the time-temperature superposition principle. The resulting master curve could be fitted by a Carreau model with n almost-equal-to 0.3 and a time constant of 110 s.