EDGE CREEP OF PREPAINTED ZN-55-PERCENT-AL COATED STEEL SHEET

被引：3
|
作者：
OKA, J
TAKASUGI, M
机构：
[1] Nippon Steel Corp, Japan
来源：
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1991年 / 77卷 / 07期
关键词：
EDGE CREEP; PREPAINTED GALVALUME; ZN-AL ALLOY COATING; CORROSION; ATMOSPHERIC EXPOSURE TEST; PRETREATMENT; COATING;
D O I：
10.2355/tetsutohagane1955.77.7_1130
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The effects of pretreatments and paint coatings on the edge creep performance of prepainted Galvalume were studied by means of salt spray test and outdoor exposure test. Edge creep progress behavior in salt spray test was different from that in outdoor exposure test. According to the results of outdoor exposure test for up to 10 years, the edge creep of prepainted Galvalume is more appreciable than that of the prepainted galvanized steel sheet in the early stages of exposure. However, the edge creep rate of prepainted Galvalume decreases with the lapse of time while that of prepainted galvanized steel sheet is kept almost constant. As the results, edge creep width becomes larger in galvanized steel sheet than in Galvalume in 7 to 9 years of exposure. Meanwhile in salt spray test, edge creep width of prepainted galvanized steel sheet does not exceed that of prepainted Galvalume up to 1 000 h of exposure. Effects of pretreatments and coatings were not clearly noticed except that special primer for Galvalume decreased edge creep width of prepainted Galvalume in salt spray test.
引用
收藏
页码：1130 / 1137
页数：8
相关论文
共 50 条
  • [31] BLACK PATINA DEVELOPED ON ZN-AL ALLOY COATED STEEL SHEET
    UCHIDA, Y
    KODA, M
    FUKUI, Y
    HIROSE, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (08): : 1013 - 1020
  • [32] CHROMATE PASSIVATION PROTECTION OF ZN-COATED AND AL-ZN-COATED STEEL SHEET AGAINST WET STORAGE STAIN
    TOWNSEND, HE
    ZOCCOLA, JC
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1977, 124 (08) : C283 - C283
  • [33] Effect of Environmental Conditions on the Corrosion near Shear Cut Edge of 55 mass% Al-Zn Alloy Coated Steel Sheets
    Matsumoto, Masamitsu
    Okada, Nobuhiro
    Nishihara, Katsuhiro
    Kimoto, Masanari
    Kudo, Takeo
    Fujimoto, Shinji
    ISIJ INTERNATIONAL, 2011, 51 (03) : 462 - 470
  • [34] Influence of an annealing heat treatment on the microstructure, ductility, and corrosion resistance of a chromated 55 wt.% Al-Zn coated steel sheet
    Nogueira, TMC
    Cruz, MAS
    Rios, PR
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2001, 10 (03) : 314 - 319
  • [35] Influence of an annealing heat treatment on the microstructure, ductility, and corrosion resistance of a chromated 55 wt.% Al-Zn coated steel sheet
    T. M. C. Nogueira
    M. A. S. Cruz
    P. R. Rios
    Journal of Materials Engineering and Performance, 2001, 10 : 314 - 319
  • [36] Long-term atmospheric corrosion rates of Zn55Al-coated steel
    Thierry, Dominique
    Persson, Dan
    LeBozec, Nathalie
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2024, 75 (06): : 694 - 704
  • [37] Study on Hot dip and Coating Structure of 55% Al-Zn Alloy Coated Steel
    Leng, Yanhong
    Feng, Yunli
    Song, Meng
    ADVANCED MATERIALS, PTS 1-3, 2012, 415-417 : 276 - +
  • [38] Evaluation of chromate passivation and chromate conversion coating on 55% Al-Zn coated steel
    Rocco, AM
    Nogueira, TMC
    Simao, RA
    Lima, WC
    SURFACE & COATINGS TECHNOLOGY, 2004, 179 (2-3): : 135 - 144
  • [39] CHROMATE PASSIVATION PROTECTION OF ZN-COATED AND AL-ZN-COATED STEEL SHEET AGAINST WET-STORAGE STAIN
    TOWNSEND, HE
    ZOCCOLA, JC
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1978, 125 (08) : 1290 - 1292
  • [40] Atmospheric corrosion resistance of steel sheet coated with 5% Al-Zn plus mischmetal
    Townsend, HE
    MATERIALS PERFORMANCE, 2005, 44 (11) : 28 - 31
12345