IMPROVING STABILITY IN THE DOUBLE-CANTILEVER-BEAM FRACTURE TEST

被引：1
|
作者：
WETHERHOLD, RC
FORAND, JA
机构：
[1] Department of Mechanical and Aerospace Engineering, State University of New York at Buffalo, Buffalo
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1991年 / 147卷 / 01期
关键词：
D O I：
10.1016/0921-5093(91)90816-6
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The double-cantilever-beam test is typical of traditional fracture tests used to determine critical stress intensity factor or critical energy release rates. In its basic fixed-grip configuration, it should allow a number of data points to be taken during a slow controlled crack propagation. Machine compliance and initial machined-notch bluntness may, however, cause the crack to propagate catastrophically in brittle materials. This letter deals with the use of externally applied closure forces to improve the crack growth stability in brittle materials.
引用
收藏
页码：L17 / L20
页数：4
相关论文
共 50 条
  • [41] MIXED-MODE FRACTURE OF BONDED JOINTS USING THE ASYMMETRIC TAPERED DOUBLE-CANTILEVER BEAM TEST
    Nunes, F. A. A.
    Campilho, R. D. S. G.
    IRF2018: PROCEEDINGS OF THE 6TH INTERNATIONAL CONFERENCE ON INTEGRITY-RELIABILITY-FAILURE, 2018, : 313 - 314
  • [42] Comparative evaluation of the Double-Cantilever Beam and Tapered Double-Cantilever Beam tests for estimation of the tensile fracture toughness of adhesive joints
    Lopes, R. M.
    Campilho, R. D. S. G.
    da Silva, F. J. G.
    Faneco, T. M. S.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2016, 67 : 103 - 111
  • [43] Large Displacement Aspects on Fracture Testing with Double Cantilever Beam Specimens
    Fred Nilsson
    International Journal of Fracture, 2006, 139 : 305 - 311
  • [44] FRACTURE PROPERTIES OF FERROCEMENT USING DOUBLE CANTILEVER BEAM SPECIMENS.
    Desayi, P.
    Ganesan, N.
    International journal of cement composites and lightweight concrete, 1986, 8 (02): : 121 - 132
  • [45] Nonlinear Fracture Dynamic Analysis of Double Cantilever Beam Sandwich Specimens
    Burlayenko, Vyacheslav N.
    Sadowski, Tomasz
    Dimitrova, Svetlana D.
    NEW TRENDS IN NONLINEAR DYNAMICS, VOL III: PROCEEDINGS OF THE FIRST INTERNATIONAL NONLINEAR DYNAMICS CONFERENCE (NODYCON 2019), 2020, : 89 - 97
  • [46] Stress corrosion cracking of alloy C-22 and Ti Gr-12 using double-cantilever-beam technique
    Roy, AK
    Fleming, DL
    Freeman, DC
    Lum, BY
    MICRON, 1999, 30 (06) : 649 - 654
  • [47] DETERMINING THE CRITICAL STRAIN-ENERGY RELEASE RATE OF PLASMA-SPRAYED COATINGS USING A DOUBLE-CANTILEVER-BEAM TECHNIQUE
    OSTOJIC, P
    MCPHERSON, R
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1988, 71 (10) : 891 - 899
  • [48] Comparison of Cyclic and Monotonic Loading of a Double Cantilever Beam Adhesion Test
    Budzik, Michal K.
    Jumel, Julien
    Ben Salem, Naoufel
    Shanahan, Martin E. R.
    JOURNAL OF ADHESION, 2014, 90 (03): : 252 - 267
  • [49] Sensitivity of double cantilever beam test to surface contamination and surface pretreatment
    Wetzel, M.
    Holtmannspoetter, J.
    Gudladt, H. -J.
    Czarnecki, J. V.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2013, 46 : 114 - 121
  • [50] Effect of adhesion defects on crack propagation in double cantilever beam test
    Ali, Mahfoudh Taleb
    Jumel, Julien
    Shanahan, Martin E. R.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2018, 84 : 420 - 430
12345