A NEW TENTATIVE PHASE-EQUILIBRIUM DIAGRAM FOR THE ZRO2-CEO2 SYSTEM IN AIR

被引:138
|
作者
DURAN, P
GONZALEZ, M
MOURE, C
JURADO, JR
PASCUAL, C
机构
[1] Electroceramics Department, Instituto de Ceramica y Vidrio (CSIC), Arganda del Rey, Madrid
关键词
D O I
10.1007/BF00580121
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The phase relationships over a wide range of temperature and compositions in the ZrO2-CeO2 system have been reinvestigated. From DTA results, thermal expansion measurements and KIC determinations it was established that additions of CeO2 to ZrO2 decreases the monoclinic to tetragonal ZrO2 transition temperature, from 990 ° C to 150 ∓ 50 ° C, and an invariant eutectoid point at approximately 15 mol% CeO2 exists. The extent of the different single- and two-phase fields were determined with precise lattice parameter measurements on quenched samples. Evidence for the existence of a binary compound Ce2Zr3O10 (ø-phase) was obtained by X-ray diffraction. The ø-phase was stable below approximately 800 ° C, above which it decomposes into tetragonal zirconia + fluorite ceria solid solutions. Taking into account the polymorphic tetragonal-cubic transition and the narrowness of the two-phase tetragonal zirconia + fluorite ceria field above 2000 ° C, the existence of a new invariant eutectoid point was assumed, in which the metastable fluorite zirconia solid solution decomposes into tetragonal zirconia + fluorite ceria solid solutions. From the results obtained, the phase diagram also incorporates a eutectic point located at approximately 2300 ° C and 24 mol % CeO2. © 1990 Chapman and Hall Ltd.
引用
收藏
页码:5001 / 5006
页数:6
相关论文
共 50 条
  • [21] Phase diagram calculation of the ZrO2-CeO2-YO1.5 system
    Yokokawa, H
    Horita, T
    Sakai, N
    Dokiya, M
    VanHerle, J
    Kim, SG
    DENKI KAGAKU, 1996, 64 (06): : 690 - 691
  • [22] HYDRATION AND PHASE-EQUILIBRIUM STUDIES IN THE SYSTEM SRO-ZRO2-MGO
    GARG, RK
    SEMLER, CE
    AMERICAN CERAMIC SOCIETY BULLETIN, 1979, 58 (03): : 352 - 352
  • [23] Preparation of ZrO2-CeO2 and HfO2-CeO2 nanopowders
    V. B. Glushkova
    T. I. Panova
    Inorganic Materials, 2006, 42 : 1076 - 1082
  • [24] PHASE-EQUILIBRIUM DIAGRAM OF SYSTEM NA2S4-S
    CLEAVER, B
    HAMES, MD
    WADSLEY, M
    TRANSACTIONS OF THE INSTITUTION OF MINING AND METALLURGY SECTION C-MINERAL PROCESSING AND EXTRACTIVE METALLURGY, 1976, 85 (DEC): : C218 - C219
  • [25] Preparation of ZrO2-CeO2 and HfO2-CeO2 nanopowders
    Glushkova, V. B.
    Panova, T. I.
    INORGANIC MATERIALS, 2006, 42 (10) : 1076 - 1082
  • [26] MICROSTRUCTURE AND PHASE-COMPOSITION OF ZRO2-CEO2 THERMAL BARRIER COATINGS
    HARMSWORTH, PD
    STEVENS, R
    JOURNAL OF MATERIALS SCIENCE, 1991, 26 (15) : 3991 - 3995
  • [27] ON THE CUBIC TETRAGONAL PHASE-EQUILIBRIUM OF THE ZRO2-Y2O3 SYSTEM
    YOSHIKAWA, N
    EDA, H
    SUTO, H
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1986, 50 (01) : 113 - 118
  • [28] Electrical Properties of ZrO2-CeO2 at Intermediate Temperatures
    Zhu, Bin
    Luo, Xiaoguang
    Xia, Changrong
    Albinsson, I.
    Mellander, B. -E.
    IONICS, 1997, 3 (5-6) : 363 - 367
  • [29] THE CONFIRMATION OF PHASE-EQUILIBRIA IN THE SYSTEM ZRO2-CEO2 BELOW 1400-DEGREES-C
    YOSHIMURA, M
    TANI, E
    SOMIYA, S
    SOLID STATE IONICS, 1981, 3-4 (AUG) : 477 - 481
  • [30] MICROSTRUCTURAL DEVELOPMENT OF SINTERED ZRO2-CEO2 CERAMICS
    ZHOU, Y
    CERAMICS INTERNATIONAL, 1991, 17 (06) : 343 - 346