EFFECTS OF WELDING RESIDUAL-STRESSES ON FATIGUE CRACK-GROWTH BEHAVIOR IN BUTT WELDS OF A PIPELINE STEEL

In the present test the fatigue crack growth rate in the parent plate, weld and cross-bond regions was measured and the results were correlated with the stress intensity range ΔK and the effective stress intensity range ΔKeff. It is indicated that the welding residual stresses strongly affect the crack growth rate. For the weld metal and cross-bond compact tension specimens in which crack growth is along the weld line the fatigue crack growth rate increases as the crack grows. However, for the T compact tension specimen in which crack growth is perpendicular to the weld line at a constant value of applied ΔK the crack growth rate initially decreases as the crack grows. Particularly, at a low constant value of applied ΔK the crack growth rate obviously decreases and the crack fails to grow after short crack growth. When the crack grows to intersect the welded zone, the fatigue crack growth rate gradually increases as the crack grows further. It is clear that the effect of welding residual stresses on the crack growth rate is related to the position of the crack and its orientation with respect to the weld line. Finally, the models of welding residual stress redistribution in the compact tension specimens with the growing crack and its influence on the fatigue crack closure are discussed. It appears that for a butt-welded joint one of the crack closure mechanisms may be considered by the bend or rotation deformation of crack faces due to the welding residual stress redistribution as the fatigue crack grows in the welded joint. © 1990.