COKE FORMATION ON PREOXIDIZED IRON AND NICKEL IN A CH4-H2 GAS ATMOSPHERE AT 1,000-DEGREES-C

被引：15
|
作者：
TOKURA, S
OTSUKA, N
KUDO, T
机构：
[1] Sumitomo Metal Ind Ltd, Amagasaki
来源：
CORROSION | 1993年 / 49卷 / 07期
关键词：
CARBON; COKE FORMATION; CRACKING FURNACE TUBE; GRAPHITE DEPOSITION; SCALE REDUCTION;
D O I：
10.5006/1.3316085
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Coke formation on preoxidized iron (Fe) and nickel (Ni) specimen was studied in a 15% methane-hydrogen gas (CH4-H-2) atmosphere at 1,000-degrees-C by thermogravimetry. Ground specimen of different surface finish were investigated also. An accelerated heterogeneous reaction resulted when the Fe specimen were Preoxidized, resulting in a heavy coke deposition. This resulted from formation of an active ''metallic'' surface generated by the reduction of preoxidized scales For Ni specimen, acceleration resulting from preoxidation was small. The different surface activities between the preoxidized Fe and Ni specimen were not attributed to the different surface areas. Based on the test results, a practical remedy to alleviate deposition of coke in high-temperature cracking environments was proposed.
引用
收藏
页码：561 / 568
页数：8
相关论文
共 50 条
  • [41] Study on coke formation and stability of nickel-based catalysts in CO2 reforming of CH4
    Li, XC
    Wu, M
    Yang, YF
    He, F
    JOURNAL OF RARE EARTHS, 2004, 22 (06) : 854 - 858
  • [42] CARBON DEPOSITION OVER FE, NI, AND CO FOILS FROM CO-H2-CH4-CO2-H2O, CO-CO2, CH4-H2, AND CO-H2-H2O GAS-MIXTURES .1. MORPHOLOGY
    JABLONSKI, GA
    GEURTS, FW
    SACCO, A
    BIEDERMAN, RR
    CARBON, 1992, 30 (01) : 87 - 98
  • [43] Deposition of a well-adherent nano-crystalline diamond coating on titanium using CH4-H2 gas mixture
    Askari, Syed Jawid
    Lu, Fanxiu
    PRICM 6: SIXTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-3, 2007, 561-565 : 1145 - 1148
  • [44] On the mechanism of CH3 radical formation in hot filament activated CH4/H2 and C2H2/H2 gas mixtures
    Smith, JA
    Cameron, E
    Ashfold, MNR
    Mankelevich, YA
    Suetin, NV
    DIAMOND AND RELATED MATERIALS, 2001, 10 (3-7) : 358 - 363
  • [45] Coke formation during metal dusting of iron in CO-H2-H2O gas with high CO content
    Zhang, J
    Schneider, A
    Inden, G
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2003, 54 (10): : 770 - 777
  • [46] Structure of Diamond Films Grown Using High-Speed Flow of a Thermally Activated CH4-H2 Gas Mixture
    Fedoseeva, Yu, V
    Gorodetskiy, D., V
    Baskakova, K., I
    Asanov, I. P.
    Bulusheva, L. G.
    Makarova, A. A.
    Yudin, I. B.
    Plotnikov, M. Yu
    Emelyanov, A. A.
    Rebrov, A. K.
    Okotrub, A., V
    MATERIALS, 2020, 13 (01) : 219
  • [47] INFLUENCE OF REACTION RATE ON GAS CARBURIZING OF STEEL IN A CH4-H2-N2 ATMOSPHERE
    COLLIN, R
    BRACHACZ.M
    THULIN, D
    JOURNAL OF THE IRON AND STEEL INSTITUTE, 1969, 207 : 1122 - &
  • [48] Investigations on nitrogen addition in the CH4-H2 gas mixture used for diamond deposition for a better understanding and the optimisation of the synthesis process
    Bénédic, F
    Belmahi, M
    Elmazria, O
    Assouar, MB
    Fundenberger, JJ
    Alnot, P
    SURFACE & COATINGS TECHNOLOGY, 2003, 176 (01): : 37 - 49
  • [49] EXPERIMENTAL STUDIES ON THERMAL AND HYDRAULIC PERFORMANCE OF FUEL STACK OF VHTR, .4. TEST-RESULTS OF HENDEL SINGLE-CHANNEL TEST RIG WHEN HELIUM GAS WAS HEATED UP TO 1,000-DEGREES-C
    HINO, R
    TAKASE, K
    MARUYAMA, S
    IZAWA, N
    MIYAMOTO, Y
    SHIMOMURA, H
    KAWAMURA, H
    JOURNAL OF THE ATOMIC ENERGY SOCIETY OF JAPAN, 1988, 30 (04): : 343 - 349
  • [50] Effects of argon and oxygen addition to the CH4-H2 feed gas on diamond synthesis by microwave plasma enhanced chemical vapor deposition
    Han, YS
    Kim, YK
    Lee, JY
    THIN SOLID FILMS, 1997, 310 (1-2) : 39 - 46
12345