RECRYSTALLIZATION IN FIBROUS AND PARTICULATE METAL MATRIX COMPOSITES

被引：45

作者：

SHAHANI, RA

CLYNE, TW

机构：

[1] Department of Materials Science and Metallurgy, University of Cambridge, Cambridge, CB2 3QZ, Pembroke Street

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1991年 / 135卷 / 1-2期

关键词：

D O I：

10.1016/0921-5093(91)90576-9

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Recrystallization behaviour has been explored for several metal matrix composites produced by powder blending followed by extrusion. Commercial purity aluminium was used as the matrix material. The composites contain a fine dispersion of Al2O3 (inherited from the original oxide film on the aluminium powder) in addition to the reinforcement. Both the large reinforcement particles and the fine oxide dispersion influence recrystallization. Nucleation may be stimulated by the large particles, while subsequent growth of these nuclei is inhibited by the fine dispersion as a result of Zener pinning effects. In the current study, recrystallization has been monitored by optical microscopy, coupled with hardness measurements. Increasing the reinforcement content from 10 vol.% to 20 vol.% was found to increase the nucleation efficiency at the reinforcing particles, resulting in a much finer recrystallized grain size. Short fibres were found to nucleate recrystallization more efficiently than equiaxed particles.

引用

页码：281 / 285

页数：5

共 50 条

[21] Microstructure Modeling of particulate reinforced metal matrix composites
Shoukry, Samir N.
Prucz, Jacky C.
Shankaranarayana, Praveen G.
William, Gergis W.
MECHANICS OF ADVANCED MATERIALS AND STRUCTURES, 2007, 14 (06) : 499 - 510
[22] ASPECTS OF FRACTURE IN PARTICULATE REINFORCED METAL MATRIX COMPOSITES
LLOYD, DJ
ACTA METALLURGICA ET MATERIALIA, 1991, 39 (01): : 59 - 71
[23] ULTRASONIC TECHNIQUES IN EVALUATION OF METAL MATRIX PARTICULATE COMPOSITES
ROHATGI, PK
RAMAN, S
MAJUMDAR, BS
BANERJEE, A
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1990, 123 (01): : 89 - 97
[24] MICROGRAVITY PROCESSING OF PARTICULATE REINFORCED METAL MATRIX COMPOSITES
MOREL, DE
STEFANESCU, DM
CURRERI, PA
ADVANCED MATERIALS : THE BIG PAYOFF, 1989, 21 : 678 - 687
[25] Turning of particulate metal matrix composites - review and discussion
Basavarajappa, S.
Chandramohan, G.
Rao, K. V. Narasimha
Radhakrishanan, R.
Krishnaraj, V.
PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART B-JOURNAL OF ENGINEERING MANUFACTURE, 2006, 220 (07) : 1189 - 1204
[26] Quantifying the plastic anisotropy for particulate metal matrix composites
Kourkoulis, SK
ADVANCED COMPOSITES LETTERS, 2002, 11 (04) : 153 - 163
[27] Hardness and flow strength in particulate metal matrix composites
Cáceres, CH
Poole, WJ
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 332 (1-2): : 311 - 317
[28] XFEM modeling of ultrasonic wave propagation in polymer matrix particulate/fibrous composites
Liu, Zhanli
Oswald, Jay
Belytschko, Ted
WAVE MOTION, 2013, 50 (03) : 389 - 401
[29] Effect of interfacial characteristics on the mechanical performance of particulate, fibrous and layered metal matrix composites - a review of some recent work
Clyne, T.W.
Key Engineering Materials, 1997, 127-131 (Pt 1): : 81 - 98
[30] The effect of interfacial characteristics on the mechanical performance of particulate, fibrous and layered metal matrix composites - A review of some recent work
Clyne, TW
CMMC 96 - PROCEEDINGS OF THE FIRST INTERNATIONAL CONFERENCE ON CERAMIC AND METAL MATRIX COMPOSITES, PTS 1 AND 2, 1997, 127-3 : 81 - 98

← 1 2 3 4 5 →