THE HIGH-TEMPERATURE CORROSION BEHAVIOR OF VARIOUS ALLOYS AND COATINGS UNDER COAL-GASIFICATION CONDITIONS

被引：5
|
作者：
BESENICAR, S [1 ]
HAANAPPEL, NWJ [1 ]
HAANAPPEL, VAC [1 ]
FRANSEN, T [1 ]
GELLINGS, PJ [1 ]
机构：
[1] EDVARD KARDELJ UNIV,J STEFAN INST,YU-61000 LJUBLJANA,YUGOSLAVIA
来源：
MATERIALS AT HIGH TEMPERATURES | 1991年 / 9卷 / 04期
关键词：
SULFIDATION; COATINGS; ALLOYS; CORROSION;
D O I：
10.1080/09603409.1991.11689660
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The corrosion behaviour of several alloys and of various protective coatings on 15Mo3 has been tested under conditions found in coal gasification processes. The experiments showed that of all the uncoated samples tested, only AISI 310 has a promising resistance to these corrosive atmospheres. On most of the other materials spalling of the corrosion products was observed. The main corrosion products were iron, chromium and nickel sulphides, chromium oxide and chromium carbide. Materials protected by different coatings showed very good corrosion resistance when coated by plasma spraying with FeCrAl, containing small amounts of yttrium. Good resistance by coating against the corrosion was also observed for alloys chromized by pack cementation. A small amount of vanadium added to the pack improved the quality of the diffusion coating considerably.
引用
收藏
页码：193 / 200
页数：8
相关论文
共 50 条
  • [31] WHATS NEW IN HIGH-TEMPERATURE SULFUR REMOVAL SYSTEMS FOR FLUIDIZED-BED COAL-GASIFICATION
    KEAIRNS, DL
    NEWBY, RA
    ONEILL, EP
    ARCHER, DH
    [J]. JOURNAL OF THE AIR POLLUTION CONTROL ASSOCIATION, 1978, 28 (04): : 328 - 333
  • [32] COAL-GASIFICATION BY STEAM USING PROCESS HEAT FROM HIGH-TEMPERATURE NUCLEAR-REACTORS
    VANHEEK, KH
    JUNTGEN, H
    PETERS, W
    BUCHNER, G
    KALWA, G
    JAHNS, W
    WIEGAND, D
    [J]. ATOMKERNENERGIE-KERNTECHNIK, 1982, 40 (04): : 225 - 245
  • [33] Influence of intermetallide coatings on the high-temperature corrosion resistance of martencite steel in various structural conditions
    Vardanyan, E. L.
    Ramazanov, K. N.
    Agzamov, R. D.
    Yagafarov, I. I.
    Khamzina, A. R.
    Nazarov, A. Yu
    [J]. SCIENTIFIC TECHNICAL CONFERENCE ON LOW TEMPERATURE PLASMA DURING THE DEPOSITION OF FUNCTIONAL COATINGS (LTP COATINGS 2017), 2018, 1058
  • [34] PLASTIC BEHAVIOR OF COAL UNDER RAPID-HEATING HIGH-TEMPERATURE CONDITIONS
    FONG, WS
    KHALIL, YF
    PETERS, WA
    HOWARD, JB
    [J]. FUEL, 1986, 65 (02) : 195 - 201
  • [35] PLASTIC BEHAVIOR OF COAL UNDER RAPID-HEATING HIGH-TEMPERATURE CONDITIONS
    FONG, WS
    PETERS, WA
    HOWARD, JB
    [J]. ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1985, 189 (APR-): : 24 - FUEL
  • [36] THE EROSION-CORROSION OF ALLOYS UNDER OXIDIZING-SULFIDIZING CONDITIONS AT HIGH-TEMPERATURE
    STOTT, FH
    JORDAN, MP
    LEKATOS, S
    STACK, MM
    WOOD, GC
    [J]. WEAR, 1995, 186 (01) : 291 - 298
  • [37] MATERIALS FOR USE UNDER HIGH-TEMPERATURE AND CORROSION CONDITIONS
    BRILL, U
    [J]. METALL, 1995, 49 (10): : 655 - 661
  • [38] CORROSION-RESISTANCE OF HIGH-CHROMIUM STEELS IN COAL-GASIFICATION ATMOSPHERES
    KIHARA, S
    NAKAGAWA, K
    OHTOMO, A
    KATO, M
    [J]. MATERIALS PERFORMANCE, 1987, 26 (06) : 9 - 17
  • [39] CORROSION BEHAVIOR OF HIGH-TEMPERATURE ALLOYS IN IMPURE HELIUM ENVIRONMENTS
    SHINDO, M
    QUADAKKERS, WJ
    SCHUSTER, H
    [J]. JOURNAL OF NUCLEAR MATERIALS, 1986, 140 (02) : 94 - 105
  • [40] Prospects for high-temperature gasification of coal and sludge
    Bogomolov A.R.
    Shevyrev S.A.
    Alekseev M.V.
    [J]. Thermal Engineering (English translation of Teploenergetika), 2013, 60 (02): : 153 - 156
12345