FREQUENCY-DEPENDENCE OF THE COMPLEX DIELECTRIC-CONSTANT OF SODIUM CARBOXYMETHYL CELLULOSE

The dielectric constant, epsilon', and dielectric loss, epsilon'', were determined for three solid carboxymethyl cellulose samples having different levels of substitution and different degrees of polymerization over a frequency range of 0.1 - 10 000 kHz at temperatures from 10-60-degrees-C. In contrast to the two relaxation processes, gamma and beta, previously observed in native cotton cellulose, only one relaxation process within a frequency range of 0.1 - 1 kHz was identified. It was found that the dielectric properties do not only depend on the degree of substitution, but also on the weight-average degree of polymerization and uniformity of distribution.