Control of Separation and Diameter of Ag Nanorods through Self-organized Seeds

This paper proposes a mechanism of controlling the diameter and separation of metallic nanorods from physical vapor deposition through self-organized seeds and experimentally demonstrates the feasibility using Ag as the prototype metal, In as the seed and Si the substrate. Being non-wetting on Si substrates, deposited In atoms self-organize into islands. Subsequently deposited Ag atoms attach to In islands, rather than to Si substrates, due to preferential bonding and geometrical shadowing. The experimental results show that self-organized In seeds of 5 nm nominal thickness give rise to the best separation and the smallest diameter of Ag nanorods.