Effect of Silver Addition on Mechanical Properties of Melt-Processed Sm-Ba-Cu-O Bulk Superconductor

被引：0
|
作者：
Naomichi Sakai
Takeshi Miyamoto
Seok-Jong Seo
Shinya Nariki
Masato Murakami
机构：
[1] SRL/ISTEC,
来源：
Journal of Low Temperature Physics | 1999年 / 117卷
关键词：
Magnetic Field; Mechanical Property; Heat Treatment; Tensile Strength; Tensile Stress;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We have studied mechanical properties of melt-processed single-grain Sm-Ba-Cu-O (Sml23+Sm211) bulks with and without silver doping. Tensile stress is induced by thermal stress during heat treatment, and also induced by applying magnetic fields. It is found that the silver addition was effective in decreasing the thermal stress and increasing the tensile strength of the Sm-Ba-Cu-O bulk. The tensile strength of the silver doped sample was 37.4MPa, which is about one and half times larger than that of the undoped sample.
引用
收藏
页码：981 / 985
页数：4
相关论文
共 50 条
  • [31] Trapped field distribution within a cylindrical hole in Sm-Ba-Cu-O bulk superconductor
    Masuzawa, Mika
    Egawa, Kazumi
    Tsuchiya, Kiyosumi
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2006, 16 (02) : 1031 - 1034
  • [32] Melt process of Sm-Ba-Cu-O bulk superconductors by thin film cold seeding
    Fujimoto, H
    Ozaku, H
    Ohtabara, E
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 392 : 535 - 539
  • [33] The effect of Pd/Pt addition on the superconductivity of Sm-Ba-Cu-O materials
    Chen, SY
    Chen, IG
    Wu, MK
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2002, 15 (05): : 741 - 747
  • [34] The influence of a grain boundary on the thermal transport properties of bulk, melt-processed Y-Ba-Cu-O
    Marchal, C.
    Fagnard, J. F.
    Shi, Y. H.
    Cardwell, D. A.
    Mucha, J.
    Misiorek, H.
    Cloots, R.
    Vertruyen, B.
    Vanderbemden, P.
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2013, 26 (01):
  • [35] Effect of BaO2 addition on superconducting properties of melt-processed (Sm, Eu, Gd)Ba2Cu3O7-δ superconductors
    Hu, A
    Zhou, H
    Nariki, S
    Sakai, N
    Murakami, M
    Hirabayashi, I
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2004, 17 (03): : 545 - 548
  • [36] Effects of subgrains on critical current properties in melt-processed RE-Ba-Cu-O bulk superconductors
    Ogasawara, K
    Sakai, N
    Koblischka, MR
    Koblischka-Veneva, A
    Murakami, M
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2004, 17 (02): : S61 - S65
  • [37] HIGH-TEMPERATURE ANOMALIES IN SM-BA-CU-O SUPERCONDUCTOR
    HAJKO, V
    HUDAK, O
    MOLOKAC, S
    SEMAN, M
    TIMKO, M
    ZENTKO, A
    FIZIKA NIZKIKH TEMPERATUR, 1988, 14 (02): : 215 - 217
  • [38] Fabrication of melt-processed RE-Ba-Cu-O bulk superconductors with high densities
    Sakai, N
    Ogasawara, K
    Inoue, K
    Ishihara, D
    Murakami, M
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2001, 11 (01) : 3509 - 3512
  • [39] Trapped field distribution on Sm-Ba-Cu-O bulk superconductor by pulsed-field magnetization
    Yanagi, Y
    Itoh, Y
    Yoshikawa, M
    Oka, T
    Hosokawa, T
    Ishihara, H
    Ikuta, H
    Mizutani, U
    ADVANCES IN SUPERCONDUCTIVITY XII, 2000, : 470 - 472
  • [40] Flexural strength of melt-processed Y-Ba-Cu-O bulk superconductors with Ag addition measured at 77 K
    Fujimoto, H
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2003, 16 (09): : 1115 - 1119
12345