Effect of enamel coating on oxidation and hot corrosion behaviors of Ti-24Al-14Nb-3V alloy

被引：0
|
作者：
Yuming Xiong
Chunhong Guan
Shenglong Zhu
Fuhui Wang
机构：
[1] Institute of Metal Research of Chinese Academy of Sciences,State Key Laboratory for Corrosion and Protection
来源：
Journal of Materials Engineering and Performance | 2006年 / 15卷
关键词：
enamel coating; hot corrosion; oxidation; titanium aluminum intermetallics;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The effect of enamel coating on the isothermal and cyclic oxidation at 900 °C in air and on the hot corrosion resistance of Ti-24Al-14Nb-3V in both 85% Na2SO4+15%K2SO4 and 15%NaCl+85% Na2SO4 molten mixed salts at 850 °C was investigated. The results indicated that Ti-24Al-14Nb-3V alloy exhibited poor oxidation resistance due to the formation of nonprotective Al2O3+TiO2+AlNbO4 scales and poor hot corrosion resistance due to the spallation of scales formed in molten Na2SO4+K2SO4 and NaCl+Na2SO4. Enamel coating suppressed the migration of oxygen and corrosive ions into the substrate to improve the oxidation and hot corrosion resistance of Ti-24Al-14Nb-3V alloy. However, the dissolution of oxides components of the coating into the molten salts degraded enamel coating and the degradation of the coating involved a process by which Cl− anion penetrated into the substrate through voids in the coating to accelerate corrosion of Ti-24Al-14Nb-3V alloy.
引用
收藏
页码：564 / 569
页数：5
相关论文
共 50 条
  • [31] Hot Corrosion Behavior of Ti45Al8.5Nb Alloy: Effect of Anodization and Pre-oxidation
    Hao-Jie Yan
    Jun-Jie Xia
    Lian-Kui Wu
    Fa-He Cao
    Acta Metallurgica Sinica (English Letters), 2022, 35 : 1531 - 1546
  • [32] Effect of V/Nb on the Oxidation Resistance of Ti-45Al-9(V, Nb, Y) Alloy
    Chen Yuyong
    Yang Fei
    Kong Fantao
    Xiao Shulong
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 (03) : 429 - 432
  • [33] Superplastic diffusion bonding of a Ti-24Al-14Nb-3V-0.5Mo intermetallic alloy
    Zhu, HL
    Li, ZQ
    Wang, CX
    SUPERPLASTICITY IN ADVANCED MATERIALS, ICSAM-2000, 2001, 357-3 : 607 - 612
  • [34] Oxidation and electrochemical corrosion performance of Ti3Al alloy with TiAl coating
    Xi, Yan Jun
    Liu, Yong Jun
    Wang, Zhi Xin
    Liu, Jin Bin
    ANTI-CORROSION METHODS AND MATERIALS, 2010, 57 (01) : 13 - 17
  • [35] Effect of magnetron sputtered Al coating and anodization on the hot corrosion performance of Ti48Al2Nb2Cr alloy
    Li, Zhe-Xuan
    Liu, Yan-Hua
    Liu, Hui-Jun
    Wu, Lian-Kui
    Cao, Fa-He
    MATERIALS TODAY COMMUNICATIONS, 2023, 36
  • [36] Oxidation and hot corrosion behavior of Ti2AlNb-based alloy with and without enamel coating at 800 °C
    Zheng De-you
    Xiong Yu-ming
    Zhu Sheng-long
    Li Ming-sheng
    Wang Fu-hui
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 : S2050 - S2054
  • [37] Influence of an oxidation protective coating upon hot corrosion and mechanical behaviour of Ti-48Al-2Cr-2Nb alloy
    Bacos, M-P
    Thomas, M.
    Raviart, J-L
    Morel, A.
    Mercier, S.
    Josso, P.
    INTERMETALLICS, 2011, 19 (08) : 1120 - 1129
  • [38] EFFECT OF HYDROGENATION ON THE MICROSTRUCTURE OFTi-24Al-14Nb-3V-0.5Mo ALLOY
    L. Dong
    L.G. Zhou
    H. Ding and C.B. Zhang(Laboratory of Atomic Imaging of Solids
    Acta Metallurgica Sinica(English Letters), 1999, (06) : 0 - 0
  • [39] Effect of an Enamel Coating on the Oxidation and Hot Corrosion Behavior of an HVOF-Sprayed Co–Ni–Cr–Al–Y Coating
    D. Xie
    X. Xiong
    F. Wang
    Oxidation of Metals, 2003, 59 : 503 - 516
  • [40] Oxidation behavior and electrochemical corrosion performance of Ti3Al alloy with TiAl coating
    Yanjun Xi
    Yongjun Liu
    Zhixin Wang
    Jinbin Lu
    Materials Science, 2011, 46 : 841 - 846
12345