On the Role of Grain Boundary Serration in Simulated Weld Heat-Affected Zone Liquation of a Wrought Nickel-Based Superalloy

The effects of grain boundary serration on boron segregation and liquation cracking behavior in a simulated weld heat-affected zone (HAZ) of a wrought nickel-based superalloy 263 have been investigated. The serrated grain boundaries formed by the developed heat treatment were highly resistant to boron segregation; the serrated sample contained 41.6 pct grain boundaries resistant to boron enrichment as compared with 14.6 pct in the unserrated sample. During weld thermal cycle simulation, liquated grain boundaries enriched with boron were observed at the peak temperature higher than 1333 K (1060 °C) in both unserrated and serrated samples; however, serrated grain boundaries exhibited a higher resistance to liquation. The primary cause of liquation in this alloy was associated with the segregation of the melting point depressing element boron at grain boundaries. The hot ductility testing result indicated that the serrated grain boundaries showed a lower susceptibility to liquation cracking; the grain boundary serration led to an approximate 15 K decrease in the brittle temperature range. These results reflect closely a significant decrease in interfacial energy as well as a grain boundary configuration change by the serration.