Corrosion Resistance of Prestressing Steel Wires

被引：0
|
作者：
М. І. Hredil
J. Toribio
机构：
[1] University of Salamanca,
[2] E.P.S.,undefined
来源：
Materials Science | 2015年 / 50卷
关键词：
Prestressing steel; polarization curves; corrosion resistance;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The cold-drawing process is widely used for the strengthening of wires made of pearlitic steels for reinforced-concrete structures. Then the steels undergo plastic deformation and the amount of defects increases. This could worsen their corrosion resistance. In our work, the effect of cold drawing on the electrochemical behavior of pearlitic steel in alkali and neutral environments is investigated. Under passivation conditions in the environment with рН 12.5, the changes in the properties of steel are not recorded. The decrease in polarization resistance and, therefore, the acceleration of corrosion as a result of the treatment of steel is observed only in the vicinity of the corrosion potential in a 3% NaCl solution.
引用
收藏
页码：665 / 670
页数：5
相关论文
共 50 条
  • [21] Anisotropic stress corrosion cracking behaviour of prestressing steel
    Toribio, J
    Lancha, AM
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 1998, 49 (01): : 34 - 38
  • [22] High pH Corrosion of Prestressing Steel in Segregated Grout
    Bertolini, Luca
    Carsana, Maddalena
    MODELLING OF CORRODING CONCRETE STRUCTURES, 2011, 5 : 147 - 158
  • [23] Influence of drawing straining path on hydrogen damage of prestressing steel wires
    Toribio, Jesus
    Lorenzo, Miguel
    Vergara, Diego
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS X, 2012, 488-489 : 775 - +
  • [24] Environmentally-assisted fatigue crack growth in prestressing steel wires
    Toribio, J.
    Matos, J. C.
    Gonzalez, B.
    Escuadra, J.
    MATERIALS SCIENCE, 2012, 47 (06) : 764 - 772
  • [25] Environmentally-assisted fatigue crack growth in prestressing steel wires
    J. Toribio
    J. C. Matos
    B. González
    J. Escuadra
    Materials Science, 2012, 47 : 764 - 772
  • [26] Effect of Deformational Processing on Microstructure and Corrosion Resistance of Medium Carbon Steel Wires
    Irene Calliari
    Marina Polyakova
    Alexandr Gulin
    Mattia Lago
    Claudio Gennari
    Luca Pezzato
    Metallography, Microstructure, and Analysis, 2020, 9 : 323 - 336
  • [27] Corrosion resistance of steel bridge wires coated with Aluminium-Zinc alloy
    Nakamura, S.
    Miyachi, K.
    Jarwali, T.
    Suzumura, K.
    BRIDGE STRUCTURES, 2014, 10 (01) : 3 - 10
  • [28] Enhanced corrosion resistance of hard steel wires produced by electrochemical cold drawing
    Zhao, Dong
    Ye, Feng
    Unigovski, Yaakov B.
    Gutman, Emmanuel M.
    Shneck, Roni
    JOURNAL OF METALS MATERIALS AND MINERALS, 2019, 29 (03): : 10 - 16
  • [29] Hydrogen Embrittlement of Concrete Prestressing Steel Wires: Susceptibility Tests.
    Arpaia, M.
    Orsini, P.G.
    Pernice, P.
    Metallurgia Italiana, 1988, 80 (01): : 33 - 37
  • [30] Effect of Deformational Processing on Microstructure and Corrosion Resistance of Medium Carbon Steel Wires
    Calliari, Irene
    Polyakova, Marina
    Gulin, Alexandr
    Lago, Mattia
    Gennari, Claudio
    Pezzato, Luca
    METALLOGRAPHY MICROSTRUCTURE AND ANALYSIS, 2020, 9 (03) : 323 - 336
12345