Catalytic behavior of La0.6Sr0.4Co0.8Fe0.2O3 perovskite-type oxide thin films deposited on YSZ during the reaction of ethanol oxidation

被引：0
|
作者：
S. Douvartzides
C. Athanasiou
N. Georgakakis
P. Tsiakaras
机构：
[1] University of Thessalia,Department of Mechanical and Industrial Engineering
来源：
Ionics | 1998年 / 4卷
关键词：
Zirconia; Catalytic Activity; Fuel Cell; Solid Oxide Fuel Cell; Solid Oxide;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The perovskite-type oxide La0.6Sr0.4Co0.8Fe0.2O3 was studied as an ethanol oxidation catalyst-anode as a probable candidate for future application in Solid Oxide Fuel Cells (SOFCs). The investigation was carried out at atmospheric total pressure in a fully Yttria-Stabilized Zirconia (YSZ) continuous stirred tank reactor (C.S.T.R.) at a temperature range between 300–700 °C. Preliminary results show that La0.6Sr0.4Co0.8Fe0.2O3 thin films deposited on the inner bottom of the one end closed YSZ tube present: a) mediocre ethanol oxidation catalytic activity at relatively low temperature values and b) thermal stability under the experimental conditions.
引用
收藏
页码：157 / 160
页数：3
相关论文
共 50 条
  • [21] Influence of Processing Parameters on Electrophoretically Deposited La0.6Sr0.4Co0.2Fe0.8O3-δ Films
    Abd Rahman, Hamimah
    Muchtar, A.
    Muhamad, Norhamidi
    Abdullah, Huda
    FRACTURE AND STRENGTH OF SOLIDS VII, PTS 1 AND 2, 2011, 462-463 : 148 - +
  • [22] COMPOSITE La0.6Sr0.4Co0.8Fe0.2O3/Ag CATHODE FOR SOFCs WITH Ce0.8Sm0.2O1.9 ELECTROLYTE
    Mosialek, M.
    Dudek, M.
    Wojewoda-Budka, J.
    ARCHIVES OF METALLURGY AND MATERIALS, 2013, 58 (01) : 275 - 281
  • [23] Perovskite-type La0.6Sr0.4Co0.2Fe0.8O3, Ba0.5Sr0.5Co0.2Fe0.8O3, and Sm0.5Sr0.5Co0.2Fe0.8O3 cathode materials and their chromium poisoning for solid oxide fuel cells
    Shen, Fengyu
    Lu, Kathy
    ELECTROCHIMICA ACTA, 2016, 211 : 445 - 452
  • [24] Solid-state dewetting of La0.6Sr0.4CO0.2Fe0.8O3±δ thin films during annealing
    Beckel, Daniel
    Dubach, Alban
    Grundy, A. Nicholas
    Infortuna, Anna
    Gauckler, Ludwig J.
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2008, 28 (01) : 49 - 60
  • [25] La0.6Sr0.4Co0.8Fe0.2O3-delta and Fe2O3/La0.6Sr0.4Co0.8Fe0.2O3-delta Powders: XPS Characterization
    Galenda, Alessandro
    Maria Natile, Marta
    Glisenti, Antonella
    SURFACE SCIENCE SPECTRA, 2006, 13 (01): : 31 - 47
  • [26] La0.6Sr0.4Fe0.8Cu0.2O3-δ perovskite oxide as cathode for IT-SOFC
    Zhou, Qingjun
    Xu, Le
    Guo, Yajie
    Jia, Dan
    Li, Yan
    Wei, W. C. J.
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2012, 37 (16) : 11963 - 11968
  • [27] Removal of nitric oxide (NO) by perovskite-type composite catalytic thick film, La0.6Sr0.4Co0.2Fe0.8O3-δ and gadolinia-doped ceria electrolyte Gd0.2Ce0.8O2-δ
    Hwang, HJ
    Moon, JW
    Moon, J
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2005, 88 (01) : 79 - 84
  • [28] Thermoanalysis, nonstoichiometry and thermal expansion of La0.4Sr0.6Co0.2Fe0.8O3-δ, La0.2Sr0.8Co0.2Fe0.8O3-δ, La0.9Sr0.1Co1/3Fe1/3Ni1/3O3-δ and La0.6Sr0.4Co0.2Fe0.6Ni0.2O3-δ perovskites
    Swierczek, Konrad
    SOLID STATE IONICS, 2008, 179 (1-6) : 126 - 130
  • [29] An investigation of the oxygen reduction reaction mechanism of La0.6Sr0.4Co0.2Fe0.8O3 using patterned thin films
    Simrick, N. J.
    Bieberle-Huetter, A.
    Ryll, T. M.
    Kilner, J. A.
    Atkinson, A.
    Rupp, J. L. M.
    SOLID STATE IONICS, 2012, 206 : 7 - 16
  • [30] Oxygen transport in La0.6Sr0.4Co0.2Fe0.8O3-δ
    Lane, JA
    Benson, SJ
    Waller, D
    Kilner, JA
    SOLID STATE IONICS, 1999, 121 (1-4) : 201 - 208
12345