Isothermal Section of Al-Si-Ce Ternary System at 1073 K

被引：0
|
作者：
Yongping Li
Zhi Li
Yongxiong Liu
Xinming Wang
Manxiu Zhao
Fucheng Yin
机构：
[1] Xiangtan University,School of Mechanical Engineering
[2] Xiangtan University,Key Laboratory of Materials Design and Preparation Technology of Hunan Province
来源：
Journal of Phase Equilibria and Diffusion | 2014年 / 35卷
关键词：
Al-Si-Ce ternary system; phase diagram; scanning electron microscopy; x-ray diffraction;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The phase equilibria in the Al-Si-Ce ternary system at 1073 K is investigated by means of x-ray diffraction and scanning electron microscope coupled with energy dispersive spectroscopy. There exist 12 three-phase regions exist in this system and one can be deduced. One ternary compound T (Ce(AlxSi1−x)2) found in the isothermal section at 1073 K has the LaPtSi structure with a lattice parameter a = 0.4242 nm which composition span ranges from 32.1-47.8 at.%Al, 17.9-33.7 at.% Si, 33.4-34.0 at.% Ce. The maximum solubility of Al (in at.%) in CeSi2−α, CeSi, Ce5Si4, Ce3Si2 and Ce5Si3 at 1073 K is 29.3, 23.8, 2.8, 13.6 and 6.5 respectively, and the maximum solubility of Si (in at.%) in Al4Ce, Al3Ce, Al2Ce and AlCe at 1073 K is 1.4, 1.7, 1.8 and 2.1 respectively.
引用
收藏
页码：276 / 283
页数：7
相关论文
共 50 条
  • [41] Phase Equilibria of V-Si-Y Ternary System at 1073 K
    Ting Yang
    Zhi Li
    Kecheng Long
    Wei Wang
    Ya Liu
    Fucheng Yin
    Journal of Phase Equilibria and Diffusion, 2019, 40 : 247 - 253
  • [42] Experimental Investigation of the Isothermal Section in the Al-Si-Y System at 773 K
    Yang, Lu
    Qin, Haiqing
    Yang, Qingkai
    Huang, Kailin
    Lu, Zhao
    Yao, Qingrong
    Deng, Jianqiu
    Cheng, Lichun
    Huang, Caimin
    Long, Qianxin
    Wang, Jiang
    Zhou, Huaiying
    METALS, 2022, 12 (12)
  • [43] Isothermal cross-section of the ternary system Si-Co-Cr at 1423K
    Kunitsyn, IV
    Kalmykov, KB
    Dunaev, SF
    VESTNIK MOSKOVSKOGO UNIVERSITETA SERIYA 2 KHIMIYA, 1996, 37 (02): : 185 - 189
  • [44] Experimental investigation of the U-Zr-Al ternary phase diagram: Isothermal sections at 673 K and 1073 K
    Moussa, C.
    Desevedavy, F.
    Noel, H.
    Pasturel, M.
    Gouttefangeas, F.
    Dubois, S.
    Stepnik, B.
    Tougait, O.
    JOURNAL OF NUCLEAR MATERIALS, 2015, 461 : 193 - 199
  • [45] Isothermal section of Mn-Zr-Si ternary system at 600℃
    Liang, Jianlie (liangjl1971@126.com), 2016, Science Press (45):
  • [46] The isothermal section of the Ce-Co-Sb ternary system at 400 °C
    Luo, R. M.
    Liu, F. S.
    Li, J. Q.
    Feng, X. W.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 471 (1-2) : 60 - 63
  • [47] ISOTHERMAL SECTION OF THE SC-CR-SI TERNARY-SYSTEM
    KOTUR, BY
    BODAK, OI
    UKRAINSKII KHIMICHESKII ZHURNAL, 1987, 53 (02): : 151 - 153
  • [48] Phase Equilibria of V-Si-Y Ternary System at 1073K
    Yang, Ting
    Li, Zhi
    Long, Kecheng
    Wang, Wei
    Liu, Ya
    Yin, Fucheng
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2019, 40 (02) : 247 - 253
  • [49] Isothermal section of the Ni-Mn-In ternary system at 773 K
    Ao, W. Q.
    Liu, F. S.
    Li, J. Q.
    Du, Y.
    Liu, F. L.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 622 : 149 - 154
  • [50] Isothermal section of the Ce-Au-Sb system at 870 K
    Salamakha, L. P.
    Bauer, E.
    Mudryi, S. I.
    Goncalves, A. P.
    Almeida, M.
    Noel, H.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 479 (1-2) : 184 - 188
12345