The aim of this investigation was to obtain the hybrid material precursor to the naturally and abundantly available sericite, a mica-based clay; the materials were further employed in the remediation of arsenic from aqueous solutions. The study was intended to provide a cost-effective and environmentally benign treatment technology. The hybrid organo-modified sericite was obtained using hexadecyltrimethylammonium bromide (HDTMA) and alkyldimethylbenzylammonium chloride (AMBA) organic surfactants by introducing regulated doses of HDTMA or AMBA. The materials were characterized using infrared and X-ray diffraction analytical data, whereas the surface morphology was discussed by taking its SEM images. These materials were employed to assess the pre-concentration and speciation of As(III) and As(V) from aqueous solutions. The batch reactor data showed that increasing the sorptive concentration (from 1.0 to 15.0 mg/L) and pH (i.e., pH 2.0 to 10.0) caused the percent uptake of As(III) and As(V) to decrease significantly. The kinetic data showed that a sharp initial uptake of arsenic reached its equilibrium state within about 50 min of contact time, and the sorption kinetics followed a pseudo-second-order rate law both for As(III) and As(V) sorption. A 1,000 times increase in the background electrolyte concentration, i.e., NaNO3, caused a significant decrease in As(III) removal, whereas As(V) was almost unaffected, which inferred that As(III) was adsorbed, mainly by the van der Waals or even by the electrostatic attraction, whereas As(V) was adsorbed chemically and formed “inner-sphere” complexes at the solid/solution interface. The equilibrium state modeling studies indicated that the sorption data fitted well the Freundlich and Langmuir adsorption isotherms. Henceforth, the removal capacity was calculated under these equilibrium conditions. It was noted that organo-modified sericite possessed a significantly higher removal capacity compared to its virgin sericite. Between these two organo-modified sericite, the HDTMA-modified sericite possessed a higher removal capacity compared to the AMBA-modified sericite.