Fabrication of Far Red Emission Phosphors Y3Al5O12:Eu(YAG:Eu) by Co-precipitation Method

Phosphors YAG:Eu (with seven molar percent of Eu to YAG) was synthesized by the co-precipitation method using NH3 solution as a precipitating agent. X-ray diffraction (XRD) patterns show that the samples are single phase, and the crystallinity starts forming at a sintering temperature of 1000°C. The crystallinity increases with the increasing sintered temperature. XRD studies followed by Rietveld refinement confirmed the body center cubic structure of the host lattice. The crystalline YAG:Eu showed four emission bands of europium ion with the force dipole transition ascribed to 5D0–7F4 located at 710 nm as the most dominating group (far-red emission—FR). The ratio of FR/OR (far-red/orange—red) is about 1.24 in all samples.