Effects of Bi2O3, TiO2, and Bi4Ti3O12 Seeding Layers on the Structural and Electrical Properties of Bi3.25La0.75Ti3O12 Thin Films Grown by a Sol–Gel Method

被引:0
|
作者
Ling Pei
Ni Hu
Gang Deng
Yeguang Bie
Yiwan Chen
Meiya Li
机构
[1] Hubei University of Technology,School of Science
[2] Hubei University of Technology,Hubei Collaborative Innovation Center for High
[3] Wuhan University,Efficiency Utilization of Solar Energy
来源
关键词
Sol–gel preparation; seeding layers; orientation; ferroelectrics; fatigue;
D O I
暂无
中图分类号
学科分类号
摘要
Ferroelectric Bi3.25La0.75Ti3O12 (BLT) thin films with Bi2O3, TiO2, and Bi4 Ti3O12 (BTO) seeding layers were prepared on Pt/TiO2/SiO2/Si (100) substrate by a sol–gel technique. The effects of the different seeding layers on the structural and electrical properties of the BLT films were investigated. X-ray diffraction indicated that the predominant orientation of the BLT thin film on the BTO seeding layer was (117). Growth of films with the Pt/BLT/Bi2O3/Pt structure was oriented differently from that of films with the Pt/BLT/TiO2/Pt and Pt/BLT/Pt structures. In addition, in comparison with the BLT film deposited directly on Pt, the TiO2 layer substantially enhanced the leakage current resistance of the BLT film. The ferroelectric nature of the BLT thin film was substantially improved by use of a BTO seeding layer. In an applied field of 750 kV/cm, the remnant polarization (2Pr) of the Pt/BLT/BTO/Pt capacitor was 61.5 μC/cm2. After 1010 switching cycles, 2Pr of the BLT, BLT/Bi2O3, BLT/TiO2, and BLT/BTO films was degraded by approximately 13, 11, 1, and 2%, respectively, indicating that all the capacitors with the different seeding layers had good polarization fatigue characteristics.
引用
收藏
页码:2340 / 2347
页数:7
相关论文
共 50 条
  • [31] Structural and multiferroic properties of epitaxial γ-Fe2O3-BiFeO3/Bi3.25La0.75Ti3O12 composite bi-layers
    Gautreau, Olivier
    Harnagea, Catalin
    Gunawan, Lina
    Botton, Gianluigi A.
    Normandin, Francois
    Veres, Teodor
    Pintilie, Lucian
    Alexe, Marin
    Pignolet, Alain
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2008, 41 (11)
  • [32] Effect of anneling on ferroelectric properties of Bi3.25La0.75Ti3O12 thin films prepared by the sol-gel method
    Guo, DY
    Wang, YB
    Yu, J
    Gao, JX
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2005, 20 (04): : 20 - 21
  • [33] The thickness effect of Bi3.25La0.75Ti3O12 buffer layer in PbZr0.58Ti0.42O3/Bi3.25La0.75Ti3O12 (PZT/BLT) multilayered ferroelectric thin films
    Li, Jianjun
    Li, Ping
    Zhang, Guojun
    Yu, Jun
    Wu, Yunyi
    Wen, Xinyi
    THIN SOLID FILMS, 2011, 519 (18) : 6021 - 6025
  • [34] Effect of substitution of vanadium on the structure and electrical properties of Bi3.25La0.75Ti3O12 thin films
    X.J. Meng
    J.H. Ma
    J.L. Sun
    T. Lin
    J. Yu
    G.S. Wang
    J.H. Chu
    Applied Physics A, 2004, 78 : 1089 - 1091
  • [35] Synthesis and characteristics of Bi3.25La0.75Ti3O12 ferroelectric thin films by Sol-Gel technology
    Wang Hua
    Ren Ming-Fang
    ACTA PHYSICA SINICA, 2006, 55 (06) : 3152 - 3156
  • [36] Effect of annealing on ferroelectric properties of Bi3.25La0.75Ti3O12 thin films prepared by the sol-gel method
    Guo D.
    Wang Y.
    Yu J.
    Gao J.
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2005, 20 (4): : 20 - 21
  • [37] Effect of substitution of vanadium on the structure and electrical properties of Bi3.25La0.75Ti3O12 thin films
    Meng, XJ
    Ma, JH
    Sun, JL
    Lin, T
    Yu, J
    Wang, GS
    Chu, JH
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2004, 78 (07): : 1089 - 1091
  • [38] The Effect of La-Doped Bi4Ti3O12 Buffer Layer on Crystallinity and Ferroelectric Properties of PbZr0.58Ti0.42O3/Bi3.25La0.75Ti3O12 Multilayered Thin Films
    Li, Jianjun
    Wen, Xinyi
    Wu, Yunyi
    Yu, Jun
    INTEGRATED FERROELECTRICS, 2011, 124 : 170 - 177
  • [39] Effects of switching pulse width and stress on properties of Bi3.25La0.75Ti3O12 thin films
    吴秀梅
    陈华
    翟亚
    吕笑梅
    刘云飞
    朱劲松
    ChinesePhysicsB, 2010, 19 (03) : 416 - 419
  • [40] Effects of Zr substitution on structures and ferroelectric properties of Bi3.25La0.75Ti3O12 thin films
    Lv, LP
    Zhang, ST
    Wang, J
    Chen, YF
    Liu, ZG
    Zhao, XN
    Cheng, GX
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2005, 38 (09) : 1355 - 1360