Influence of the Porosity of a Plasma-Electrolytic Coating on the Corrosion Resistance of D16 Alloy

被引：0
|
作者：
M. M. Student
I. B. Ivasenko
V. M. Posuvailo
H. H. Veselivs’ka
A. Yu. Pokhmurs’kyi
Ya. Ya. Sirak
V. M. Yus’kiv
机构：
[1] Ukrainian National Academy of Sciences,Karpenko Physicomechanical Institute
[2] Brandenburgische Technische Universitat Cottbus,undefined
[3] “L’vivs’ka Politekhnika” National University,undefined
来源：
Materials Science | 2019年 / 54卷
关键词：
D16 alloy; plasma-electrolytic oxidized coatings; corrosion resistance; oxide-ceramic coatings; pores;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We study the effect of the coating thickness on the corrosion resistance and porosity of oxide-ceramic coatings on D16 alloy. The coatings were synthesized in an alkaline solution for 10, 60, and 120 min at a current density of 10 A/dm2 . As a result, the coatings with thicknesses of ∼ 8–12, 50–70, and 80–120 μm, respectively, were formed on the surface of the alloy. The corrosion resistance of the coatings was investigated in a medium of weakly acid rain and in a 3% NaCl solution in water. We established the correlation between the porosity and corrosion resistance of the coatings. The oxide-ceramic coatings synthesized on D16 alloy for 60 min have the lowest porosity and the highest corrosion resistance.
引用
收藏
页码：899 / 906
页数：7
相关论文
共 50 条
  • [11] Corrosion Resistance of D16 Alloy Depending on the Salinity and Meteorological Parameters of Coastal Atmosphere
    Panchenko, Yu. M.
    Strekalov, P. V.
    Zhilikov, V. P.
    Karimova, S. A.
    Berezina, L. G.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2012, 48 (07) : 740 - 750
  • [12] New Atmospheric Corrosion Inhibitor of D16 Aluminum Alloy
    A. M. Semiletov
    Yu. B. Makarychev
    A. A. Chirkunov
    L. P. Kazansky
    Yu. I. Kuznetsov
    Protection of Metals and Physical Chemistry of Surfaces, 2021, 57 : 1344 - 1351
  • [13] Intergranular Corrosion of Cryorolled and Aged D16 Aluminum Alloy
    Krymskiy, S. V.
    Ilyasov, R. R.
    Avtokratova, E. V.
    Sitdikov, O. Sh.
    Markushev, M. V.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2017, 53 (06) : 1091 - 1099
  • [14] Influence of ageing on the ultrasonic speed in alloy D16
    Poletika, IM
    Kulikova, OA
    Egorova, NM
    Zuyev, LB
    Perovskaya, MV
    METALLOFIZIKA I NOVEISHIE TEKHNOLOGII, 2002, 24 (06): : 849 - 855
  • [15] New Atmospheric Corrosion Inhibitor of D16 Aluminum Alloy
    Semiletov, A. M.
    Makarychev, Yu B.
    Chirkunov, A. A.
    Kazansky, L. P.
    Kuznetsov, Yu, I
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2021, 57 (07) : 1344 - 1351
  • [16] Intergranular Corrosion of Cryorolled and Aged D16 Aluminum Alloy
    S. V. Krymskiy
    R. R. Ilyasov
    E. V. Avtokratova
    O. Sh. Sitdikov
    M. V. Markushev
    Protection of Metals and Physical Chemistry of Surfaces, 2017, 53 : 1091 - 1099
  • [17] EFFECT OF STRUCTURE ON THE CORROSION PROPERTIES OF SEMIFINISHED PRODUCTS OF D16 ALLOY
    SINYAVSKII, VS
    VALKOV, VD
    PROTECTION OF METALS, 1986, 22 (03): : 297 - 300
  • [18] Corrosion resistance in simulated DMFC environment of plasma electrolytic oxidation coating prepared on aluminum alloy
    Deng, Huichao
    Ma, Zezhong
    Zhang, Xuelin
    Zhang, Yufeng
    Liu, Xiaowei
    SURFACE & COATINGS TECHNOLOGY, 2015, 269 : 108 - 113
  • [19] Intergranular corrosion of D16 aluminum alloy subjected to cryorolling and aging
    Krymskiy, S. V.
    Avtokratova, E. V.
    Sitdikov, O. Sh.
    Markushev, M. V.
    LETTERS ON MATERIALS, 2012, 2 (04): : 227 - 230
  • [20] Influence of thermocyclic treatment on the mechanical properties of D16 alloy
    Tataurova, EV
    Tarasenko, SN
    Nechai, EP
    Kazantsev, AP
    RUSSIAN METALLURGY, 1999, (05): : 86 - 90
12345