Fatigue life evaluation of welded joints considering the local multiaxial stress/strain states and numerically determined residual stresses/strains

被引：0
|
作者：
Wei Shen
Renjun Yan
Xiaoxing Wang
Enqian Liu
Lin Xu
机构：
[1] Ministry of Education,Key Laboratory of High Performance Ship Technology (Wuhan University of Technology)
[2] University of Strathclyde,Department of Naval Architecture and Marine Engineering
来源：
International Journal of Steel Structures | 2017年 / 17卷
关键词：
Welding joint; residual stress; FEA; fatigue damage; multiaxial fatigue test;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This paper puts forward a kind of calculation method of estimating fatigue crack initiation life by considering welding residual stresses as initial stresses. The numerical method could be used to quantitatively analyze the influence of residual stresses on the cumulative fatigue damage. In order to gain the distribution of weld-induced residual stresses, the FE analyses as well as measurements were carried out. Based on critical plane approach, analysis of damage parameters was performed considering both welding residual stress and biaxial loads. Subsequently, validity of the proposed numerical method is verified by analyzing fatigue test results for several typical welded joints. It is concluded that the result of the present method is closer to the experimental value than that obtained with empirical formula method in the estimation of fatigue crack initiation life of welded structures.
引用
收藏
页码：139 / 153
页数：14
相关论文
共 50 条
  • [31] Quantification of the Influence of Residual Stresses on Fatigue Strength of Al-Alloy Welded Joints by Means of the Local Strain Energy Density Approach
    Ferro, P.
    Berto, F.
    STRENGTH OF MATERIALS, 2016, 48 (03) : 426 - 436
  • [32] Quantification of the Influence of Residual Stresses on Fatigue Strength of Al-Alloy Welded Joints by Means of the Local Strain Energy Density Approach
    P. Ferro
    F. Berto
    Strength of Materials, 2016, 48 : 426 - 436
  • [33] A structural stress-based critical plane method for multiaxial fatigue life estimation in welded joints
    Jiang, C.
    Liu, Z. C.
    Wang, X. G.
    Zhang, Z.
    Long, X. Y.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2016, 39 (03) : 372 - 383
  • [34] An investigation on residual stress and fatigue life assessment of T-shape welded joints
    Samadi, Farzaneh
    Mourya, Jeetendra
    Wheatley, Greg
    Khan, Mohammed Nizam
    Nejad, Reza Masoudi
    Branco, Ricardo
    Macek, Wojciech
    ENGINEERING FAILURE ANALYSIS, 2022, 141
  • [35] The effects of residual stresses on the fatigue life of 5083-O aluminum alloy spot welded joints
    Hassanifard, Soran
    Zehsaz, Mohammad
    FATIGUE 2010, 2010, 2 (01): : 1077 - 1085
  • [36] Automated fatigue life assessment for welded cruciform joint considering welding residual stress
    Lee, TK
    Rim, CW
    Han, SH
    Lee, JH
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 2800 - 2805
  • [37] An individual fatigue assessment approach considering real notch strains and local hardness applied to welded joints
    Ladinek, M.
    Niederwanger, A.
    Lang, R.
    JOURNAL OF CONSTRUCTIONAL STEEL RESEARCH, 2018, 148 : 314 - 325
  • [38] Evaluation of fatigue life based on a modified notch strain approach considering welding residual stress relaxation
    Han, DW
    Han, SH
    Shin, BC
    Kim, JH
    PROCEEDINGS OF THE FOURTEENTH (2004) INTERNATIONAL OFFSHORE AND POLAR ENGINEERING CONFERENCE, VOL 4, 2004, : 89 - 94
  • [39] Fatigue reliability evaluation of deck-to-rib welded joints in OSD considering stochastic traffic load and welding residual stress
    Cui, Chuang
    Zhang, Qinghua
    Luo, Ying
    Hao, Hong
    Li, Jun
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 111 : 151 - 160
  • [40] Fatigue life evaluation of welded joints under multiaxial loading for different stress concepts using an extended Gough-Pollard criterion
    Bauer, N. M.
    Baumgartner, J.
    Fass, M.
    WELDING IN THE WORLD, 2024, 68 (08) : 2141 - 2155
12345