The velocity of ultrasound in low-carbon steel deformed at the low yield limit

被引：4
|
作者：
B. S. Semukhin
L. B. Zuev
K. I. Bushmeleva
机构：
来源：
Journal of Applied Mechanics and Technical Physics | 2000年 / 41卷 / 3期
关键词：
Plastic Flow; Rayleigh Wave; Yield Limit; Dependence Versus; Deformation Hardening;
D O I：
10.1007/BF02465311
中图分类号：
学科分类号：
摘要：
The variation of a thin structure upon deformation of low-carbon steel at the yield limit is analyzed. The character of the interrelationship between the stage nature of a plastic flow of low-carbon steel and the velocity of ultrasound in it is established. It is shown that the velocity of ultrasound is a parameter for obtaining additional data on the development of plastic flow. The structural changes that exert an effect on the velocity of ultrasound in the deformation that corresponds to the yield site are studied.
引用
收藏
页码：556 / 559
页数：3
相关论文
共 50 条
  • [21] Metal magnetic memory signals from surface of low-carbon steel and low-carbon alloyed steel
    董丽虹
    徐滨士
    董世运
    叶明慧
    陈群志
    王丹
    尹大伟
    JournalofCentralSouthUniversityofTechnology, 2007, (01) : 24 - 27
  • [22] Metal magnetic memory signals from surface of low-carbon steel and low-carbon alloyed steel
    Li-hong Dong
    Bin-shi Xu
    Shi-yun Dong
    Ming-hui Ye
    Qun-zhi Chen
    Dan Wang
    Da-wei Yin
    Journal of Central South University of Technology, 2007, 14 : 24 - 27
  • [23] SHORT CRACK-GROWTH CLOSE TO THE FATIGUE LIMIT IN LOW-CARBON STEEL
    KLESNIL, M
    POLAK, J
    LISKUTIN, P
    SCRIPTA METALLURGICA, 1984, 18 (11): : 1231 - 1234
  • [24] Low-temperature bainite in low-carbon steel
    Long, X. Y.
    Zhang, F. C.
    Kang, J.
    Lv, B.
    Shi, X. B.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 594 : 344 - 351
  • [25] EFFECTS OF DISLOCATION LOCKING + STRAIN AGEING ON FATIGUE LIMIT OF LOW-CARBON STEEL
    OATES, G
    WILSON, DV
    ACTA METALLURGICA, 1964, 12 (01): : 21 - &
  • [26] Strength and cracking resistance of hot-deformed steel with a low-carbon martensite structure
    Romanov, I. D.
    Shatsov, A. A.
    Kleiner, L. M.
    PHYSICS OF METALS AND METALLOGRAPHY, 2013, 114 (10): : 860 - 867
  • [27] EFFECTIVENESS OF INHIBITORS IN THE HYDROGEN IMPREGNATION OF LOW-CARBON STEEL BEING ELASTICALLY DEFORMED.
    Shein, A.B.
    Soviet materials science, 1985, 21 (03): : 284 - 287
  • [28] Strength and cracking resistance of hot-deformed steel with a low-carbon martensite structure
    I. D. Romanov
    A. A. Shatsov
    L. M. Kleiner
    The Physics of Metals and Metallography, 2013, 114 : 860 - 867
  • [29] SOLUBILITY OF CARBON IN COMMERCIAL LOW-CARBON STEEL
    ROBINSON, PM
    RICHARDS, PN
    JOURNAL OF THE IRON AND STEEL INSTITUTE, 1965, 203 : 621 - &
  • [30] MELTING OF LOW-CARBON STEEL IN CONVERTERS
    SHULKIN, ML
    ZINCHENKO, SD
    SINELNIKOV, VA
    IVANOV, RM
    ABEZGAUZ, MV
    STEEL IN THE USSR, 1982, 12 (09): : 409 - 411
12345