High-Efficiency White Light Emission Using a Phosphorescent Sensitizer in Organic Light-Emitting Devices

We have fabricated white organic light-emitting devices by using the phosphorescent material fac tris (2-phenylpyridine) iridium [Ir(ppy3)] as a sensitizer, as a result, the efficiency of these devices is improved dramatically. Ir(ppy)3 and the fluorescent dye 4-(dicyanomethylene)-2-t-butyl-6-(1,1,7,7- tetramethyljulolidyl-9-enyl)(DCJTB) are co-doped into 4,4′-N,N′-dicarbazole-biphenyl (CBP) host, whose thickness affects both color and efficiency of the devices. Tris (8-hydroxyquinoline) aluminum (Alq) and 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline (bathocuproine or BCP) are used as electron-transporting and exciton-blocking layers, respectively, and N,N′-diphenyl-N,N′-bis(1-naphthyl)-(1,1′-biphenyl)-4,4′-diamine (NPB) as a blue light-emitting as well as hole-transporting layer. The maximum efficiencies of the devices with 15 and 20 nm co-doped BCP tuning layer are 7.5 and 8.6 cd/A, respectively, and the former presents fairly pure white emission with CIE coordinates of (0.33, 0.32) at 10 V, which is very stable at various biases (10–19 V).