Very low resistance ohmic contacts to n-GaN

Ohmic contacts with low resistance are fabricated on n-GaN films using Al/Ti bilayer metallization. GaN films used are 0.3 µm thick layers with carrier concentrations of 1 × 1019 cm−3 grown on the c-plane sapphire by ion-removed electron cyclotron resonance molecular beam epitaxy. The lowest value for the specific contact resistivity (ρc) of 1.2×10−8 Ω·cm2 was obtained with furnace annealing at 500°C for 60 min. This result shows the effectiveness of high carrier concentration GaN layers and the low temperature annealing for the realization of low resistance ohmic contacts. Sputtering Auger electron spectroscopy analysis reveals that Al diffuses into Ti layer and comes into contact with the GaN surface.