Studies on the curing kinetics of epoxy resins using mixture of nadic/or maleic anhydride and 4,4′-diaminodiphenyl sulfone

Curing kinetics of diglycidyl ether of bisphenol-A (DGEBA) in the presence of maleic anhydride (MA)/or nadic anhydride (NA) or mixture of MA/NA: 4,4′-diaminodiphenyl sulfone (DDS) in varying molar ratios were investigated using differential scanning calorimetry. Curing behaviour of DGEBA in the presence of varying amounts of DDS:MA/NA was evaluated by recording DSC scans at heating rates of 5, 10, 15 and 20°C min−1. The peak exotherm temperature depends on the heating rate, structure of the anhydride as well as on the ratio of anhydride: DDS. Thermal stability of the isothermally cured resins was evaluated by thermogravimetry. The char yield was highest in case of resins cured using mixture of DDS:MA (0.75:0.25; sample EM-1) and DDS:NA (0.75:0.25, sample EN-1).