Dynamic Recrystallization Behavior in Mn-Cr Gear Steel

被引：0
|
作者：
Bing-xin Wang
Xu-dong Xu
Xiang-hua Liu
Guo-dong Wang
机构：
[1] Liaoning University of Petroleum and Chemical Technology,Department of Mechanical Engineering
[2] Northeastern University,State Key Laboratory of Rolling and Automation
来源：
Journal of Iron and Steel Research International | 2006年 / 13卷
关键词：
gear steel; deformation condition; dynamic recrystallization;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Using a Gleeble 1500 hot simulator, the dynamic recrystallization (DRX) behavior of Mn-Cr type gear steel was investigated. The experimental results show that the Mn-Cr gear steel exhibits a typical DRX behavior at higher deformation temperature, lower strain rate and smaller initial austenite grain size. The DRX takes place under the conditions that Zener-Hollomon parameter (Z) is less than a critical value Zc. The DXR grains are formed by the bulging mechanism. Activation energy and stress exponent were calculated to be 378. 6 kJ · mol−1 and 5. 8 respectively by regression analysis.
引用
收藏
页码：49 / 53
页数：4
相关论文
共 50 条
  • [41] Investigation on grinding-induced dynamic recrystallization behavior of 40Cr alloy steel
    Yao, Yunlong
    Xiu, Shichao
    Sun, Cong
    Kong, Xiangna
    Hong, Yuan
    JOURNAL OF ALLOYS AND COMPOUNDS, 2021, 867
  • [42] Dynamic Recrystallization Behavior of 13%Cr Martensitic Stainless Steel under Hot Working Condition
    Ebrahimi, G. R.
    Keshmiri, H.
    Maldar, A. R.
    Momeni, A.
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2012, 28 (05) : 467 - 473
  • [43] Dynamic Recrystallization Behavior of a Fe-Cr-Ni Super-Austenitic Stainless Steel
    Asli, A. Hoseini
    Zarci-Hanzaki, A.
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2009, 25 (05) : 603 - 606
  • [44] Effect of electron-beam irradiation temperature on irradiation damage of high Mn-Cr steel
    Bae, DS
    Nahm, SH
    Lee, HM
    Kinoshita, H
    Shibayama, T
    Takahashi, H
    JOURNAL OF NUCLEAR MATERIALS, 2004, 329 : 1038 - 1042
  • [45] Compositional boundary between primary austenitic and ferritic Mn-Cr and Ni-Cr steel weld metals
    Diez, Fernando Martinez
    Liu, Stephen
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 452 : 1 - 7
  • [46] Dynamic recrystallization behavior and mechanism of Fe-Cr-Ni-Mn-Mo-N low magnetic stainless steel during hot deformation
    Dong, Jingbo
    Li, Kun
    Shao, Zhibao
    Peng, Lianggui
    Li, Changsheng
    JOURNAL OF MATERIALS SCIENCE, 2023, 58 (40) : 15845 - 15860
  • [47] Hot deformation behavior and dynamic recrystallization of Mn18Cr18N steel with as-cast versus wrought starting structures
    Chen Huiqin
    He Wenwu
    Zhao Xiaodong
    Qin Fengming
    Wang Zhenxing
    INTERNATIONAL CONFERENCE ON THE TECHNOLOGY OF PLASTICITY, ICTP 2017, 2017, 207 : 1791 - 1796
  • [48] Nanoparticles Reinforcement for the Improved Strength and High-Temperature Wear Resistance of Mn-Cr Steel
    A. Kračun
    D. Jenko
    M. Godec
    S. V. Savilov
    G. Prieto
    W. Tuckart
    B. Podgornik
    Metallurgical and Materials Transactions A, 2018, 49 : 5683 - 5694
  • [49] Nanoparticles Reinforcement for the Improved Strength and High-Temperature Wear Resistance of Mn-Cr Steel
    Kracun, A.
    Jenko, D.
    Godec, M.
    Savilov, S., V
    Prieto, G.
    Tuckart, W.
    Podgornik, B.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2018, 49A (11): : 5683 - 5694
  • [50] Mn-Cr isotope systematics of the D'Orbigny angrite
    Glavin, DP
    Kubny, A
    Jagoutz, E
    Lugmair, GW
    METEORITICS & PLANETARY SCIENCE, 2004, 39 (05) : 693 - 700
12345