Thermodynamic estimation on the reduction behavior of iron-chromium ore with carbon

被引：0
|
作者：
Mitsutaka Hino
Tetsuya Nagasaka
Kenichi Higuchi
Shiro Ban-Ya
机构：
[1] Tohoku University,the Department of Metallurgy, Graduate School of Engineering
[2] R&D Bureau,the Ironmaking Laboratory
[3] Nippon Steel Corporation,undefined
[4] Akita National College of Technology,undefined
来源：
Metallurgical and Materials Transactions B | 1998年 / 29卷
关键词：
Material Transaction; Reduction Behavior; JANAF Thermochemical Table; Liquid Silver; Structure Solid Solution;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The thermodynamics for reduction of iron-chromium ore by carbon is discussed. The thermodynamic properties of iron-chromium ore were evaluated from our previous work on the activities of constituents in the FeO·Cr2O3-MgO·Cr2O3-MgO·Al2O3 iron-chromite spinel-structure solid solution saturated with (Cr, Al)2O3, and those of the Fe-Cr-C alloy were estimated by a sublattice model. The stability diagrams were drawn for carbon reduction of pure FeO · Cr2O3, (Fe0.5Mg0.5)O·(Cr0.8Al0.2)2O3 iron-chromite solid solution, and South African iron-chromium ore. The evaluated stability diagrams agreed well with the literature data. It was concluded that the lowest temperature for reduction of FeO · Cr2O3 in the iron-chromium ore was 1390 K and a temperature higher than 1470 K would be necessary to reduce Cr2O3 in MgO·(Cr,Al)2O3 in the prereduction process of iron-chromium ore. The composition of liquid Fe-Cr-C alloy in equilibrium with iron-chromium ore was also estimated under 1 atm of CO at steelmaking temperature. The predicted metal composition showed reasonable agreement with the literature values.
引用
收藏
页码：351 / 360
页数：9
相关论文
共 50 条
  • [21] AGEING OF IRON-CHROMIUM ALLOYS
    VINTAYKIN, YZ
    KOLONTSO.VY
    [J]. PHYSICS OF METALS AND METALLOGRAPHY-USSR, 1968, 26 (02): : 97 - +
  • [22] THERMODYNAMIC AND ELECTROCHEMICAL STUDY OF CHEMICAL ADSORPTION OF OXYGEN AND SULFUR ON IRON-CHROMIUM ALLOYS
    OUDAR, J
    BARBOUTH, N
    BENARD, J
    [J]. MEMOIRES SCIENTIFIQUES DE LA REVUE DE METALLURGIE, 1975, 72 (09): : 649 - 659
  • [23] THERMODYNAMIC PROPERTIES OF IRON-CHROMIUM ALLOYS .2. PHASE-EQUILIBRIA
    ZAITSEV, AI
    ZEMCHENKO, MA
    MOGUTNOV, BM
    [J]. ZHURNAL FIZICHESKOI KHIMII, 1990, 64 (05): : 1195 - 1202
  • [24] IRON-CHROMIUM, IRON-CHROMIUM-NICKEL AND RELATED ALLOYS
    STRAUSS, J
    NEWELL, HD
    [J]. PROCEEDINGS-AMERICAN SOCIETY FOR TESTING AND MATERIALS, 1950, 50 : 126 - 129
  • [25] IRON-CHROMIUM, IRON-CHROMIUM-NICKEL AND RELATED ALLOYS
    STRAUSS, J
    [J]. PROCEEDINGS-AMERICAN SOCIETY FOR TESTING AND MATERIALS, 1951, 51 : 128 - 132
  • [26] THE PASSIVITY OF IRON-CHROMIUM ALLOYS
    KIRCHHEIM, R
    HEINE, B
    FISCHMEISTER, H
    HOFMANN, S
    KNOTE, H
    STOLZ, U
    [J]. CORROSION SCIENCE, 1989, 29 (07) : 899 - 917
  • [27] SPINODAL DECOMPOSITION IN IRON-CHROMIUM
    LASALLE, JC
    SCHWARTZ, LH
    [J]. JOURNAL OF METALS, 1982, 34 (08): : 34 - 34
  • [28] THE IRON-CHROMIUM REDOX BATTERY
    HAGEDORN, NH
    [J]. ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1983, 186 (AUG): : 28 - INDE
  • [29] Embedded-atom potential for an accurate thermodynamic description of the iron-chromium system
    Eich, S. M.
    Beinke, D.
    Schmitz, G.
    [J]. COMPUTATIONAL MATERIALS SCIENCE, 2015, 104 : 185 - 192
  • [30] IRON-CHROMIUM, IRON-CHROMIUM-NICKEL AND RELATED ALLOYS
    STRAUSS, J
    [J]. PROCEEDINGS-AMERICAN SOCIETY FOR TESTING AND MATERIALS, 1952, 52 : 128 - 132
12345