Thermodynamic estimation on the reduction behavior of iron-chromium ore with carbon

被引：0
|
作者：
Mitsutaka Hino
Tetsuya Nagasaka
Kenichi Higuchi
Shiro Ban-Ya
机构：
[1] Tohoku University,the Department of Metallurgy, Graduate School of Engineering
[2] R&D Bureau,the Ironmaking Laboratory
[3] Nippon Steel Corporation,undefined
[4] Akita National College of Technology,undefined
来源：
Metallurgical and Materials Transactions B | 1998年 / 29卷
关键词：
Material Transaction; Reduction Behavior; JANAF Thermochemical Table; Liquid Silver; Structure Solid Solution;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The thermodynamics for reduction of iron-chromium ore by carbon is discussed. The thermodynamic properties of iron-chromium ore were evaluated from our previous work on the activities of constituents in the FeO·Cr2O3-MgO·Cr2O3-MgO·Al2O3 iron-chromite spinel-structure solid solution saturated with (Cr, Al)2O3, and those of the Fe-Cr-C alloy were estimated by a sublattice model. The stability diagrams were drawn for carbon reduction of pure FeO · Cr2O3, (Fe0.5Mg0.5)O·(Cr0.8Al0.2)2O3 iron-chromite solid solution, and South African iron-chromium ore. The evaluated stability diagrams agreed well with the literature data. It was concluded that the lowest temperature for reduction of FeO · Cr2O3 in the iron-chromium ore was 1390 K and a temperature higher than 1470 K would be necessary to reduce Cr2O3 in MgO·(Cr,Al)2O3 in the prereduction process of iron-chromium ore. The composition of liquid Fe-Cr-C alloy in equilibrium with iron-chromium ore was also estimated under 1 atm of CO at steelmaking temperature. The predicted metal composition showed reasonable agreement with the literature values.
引用
收藏
页码：351 / 360
页数：9
相关论文
共 50 条
  • [1] Thermodynamic estimation on the reduction behavior of iron-chromium ore with carbon
    Hino, M
    Higuchi, K
    Nagasaka, T
    Ban-Ya, S
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1998, 29 (02): : 351 - 360
  • [2] THERMODYNAMIC ANALYSIS OF THE BEHAVIOR OF OXYGEN IN IRON-CHROMIUM MELTS ALLOYED WITH TITANIUM AND ALUMINUM
    LEONOVICH, BI
    MIKHAYLOV, GG
    KHASIN, GA
    [J]. RUSSIAN METALLURGY, 1980, (03): : 49 - 53
  • [3] CARBON DIFFUSIVITY IN IRON-CHROMIUM ALLOYS
    BLAZEK, KE
    COST, JR
    [J]. TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1976, 17 (10): : 630 - 636
  • [4] DETERMINATION OF SOLUBILITY OF CARBON IN IRON-CHROMIUM ALLOYS
    COST, JR
    BLAZEK, KE
    [J]. TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1975, 16 (03): : 177 - 179
  • [5] BEHAVIOR OF NITROGEN IN MOLTEN IRON-CHROMIUM ALLOYS
    TORKHOV, GF
    [J]. AUTOMATIC WELDING USSR, 1971, 24 (10): : 17 - &
  • [6] HOT HARDNESS BEHAVIOR OF IRON-CHROMIUM ALLOYS
    TEDMON, CS
    WESTBROO.JH
    [J]. ASM TRANSACTIONS QUARTERLY, 1967, 60 (03): : 442 - &
  • [7] Rate of reduction of chromium ore by liquid iron containing carbon and silicon
    Nakasuga, T
    Sun, HP
    Nakashima, K
    Mori, K
    [J]. TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2000, 86 (08): : 499 - 506
  • [8] EFFECT OF CARBON ON ELECTROCHEMICAL BEHAVIOUR OF IRON-CHROMIUM ALLOYS
    HEUMANN, T
    ROCKEL, M
    [J]. ARCHIV FUR DAS EISENHUTTENWESEN, 1971, 42 (02): : 111 - &
  • [9] EFFECT OF MOLYBDENUM ON CORROSION BEHAVIOR OF IRON-CHROMIUM ALLOYS
    ROCKEL, MB
    [J]. CORROSION, 1973, 29 (10) : 393 - 396
  • [10] CHEMICAL DIFFUSION IN IRON-CHROMIUM AND IRON-CHROMIUM-CARBON ALLOYS IN AUSTENITE RANGE
    HARTL, M
    WEVER, H
    [J]. ARCHIV FUR DAS EISENHUTTENWESEN, 1973, 44 (05): : 381 - 383
12345