Effect of Firing Temperature and Gas Atmosphere on Acid-Resistant Material Pore Structure Formation

被引：0
|
作者：
E. S. Abdrakhimova
V. Z. Abdrakhimov
机构：
[1] FGBOU VPO S. P. Korolev Samara State Aerospace University (S. P. Korolev National Research University),
[2] FGBOU VPO Samara State Economic University,undefined
来源：
Refractories and Industrial Ceramics | 2016年 / 57卷
关键词：
argillaceous part of zircon-ilmenite ore gravitation tailings (ZIG); feldspar concentrate (FSC); pyrophyllite; acid-resistant material; pore structure;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A dependence is established for acid-resistant material pore structure on firing temperature and gas parameters. It is expedient to fire acid-resistant materials up to 1100°C in an oxidizing atmosphere, and at 1100 – 1200°C in a reducing atmosphere. With this regime firing provides an improvement for acid-resistant material pore structure.
引用
收藏
页码：59 / 64
页数：5
相关论文
共 50 条
  • [41] Study of Acid-Resistant Material Properties Based on Noferrous Metallurgy Waste Using Regresssion Analysis
    E. S. Abdrakhimova
    Refractories and Industrial Ceramics, 2016, 56 : 510 - 516
  • [42] Heating Rate Effect on Gas Permeability and Pore Structure of Mortar under High Temperature
    Chen, Wei
    Liu, Yuehan
    Sheng, Mingquan
    Zhang, Hejun
    Liang, Yue
    Skoczylas, Frederic
    MATERIALS, 2022, 15 (19)
  • [43] Experimental study of physicochemical processes during firing of acid-resistant materials based on traditional natural materials and production wastes
    Abdrakhimova, E. S.
    Abdrakhimov, V. Z.
    Roshchupkina, I. Yu
    Myshentseva, Yu B.
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2012, 53 (01) : 40 - 45
  • [44] EFFECT OF ATMOSPHERE ON THE GOETHITE DECOMPOSITION AND PORE STRUCTURE OF PRODUCT PARTICLES
    HIROKAWA, S
    NAITO, T
    YAMAGUCHI, T
    JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1986, 112 (01) : 268 - 273
  • [45] Physicochemical Processes in the Firing of Acid-Resistant Materials Based on Unenriched Kaolin and High-Alumina Ferrochrome Production Slag
    Abdrakhimov, V. Z.
    Abdrakhimova, E. S.
    THEORETICAL FOUNDATIONS OF CHEMICAL ENGINEERING, 2024, 58 (01) : 144 - 151
  • [46] EFFECT OF FIRING TEMPERATURE ON THE STRUCTURE OF NICALON SIC FIBERS
    WILLIAMS, RM
    JUTERBOCK, BN
    SHINOZAKI, S
    MINDROIU, VE
    AMERICAN CERAMIC SOCIETY BULLETIN, 1984, 63 (08): : 1013 - 1013
  • [47] Pore formation in polystyrene fiber by superimposing temperature and relative humidity of electrospinning atmosphere
    Fashandi, H.
    Karimi, M.
    POLYMER, 2012, 53 (25) : 5832 - 5849
  • [48] Effect of Temperature on Pore Structure and Strength of Concrete
    Shen, Jiarong
    Xu, Qianjun
    Li, Qingbin
    ACI MATERIALS JOURNAL, 2020, 117 (01) : 85 - 95
  • [49] Effect of temperature on pore structure and strength of concrete
    Shen, Jiarong
    Xu, Qianjun
    Li, Qingbin
    1600, American Concrete Institute (117): : 85 - 95
  • [50] Formation of structure and closed porosity under high-temperature firing of granules of porous glass-ceramic material
    Apkaryan A.S.
    Kulkov S.N.
    Inorganic Materials: Applied Research, 2018, 9 (2) : 286 - 290
12345