The effect of residual stresses induced by prestraining on fatigue life of notched specimens

被引：0
|
作者：
R. Sadeler
A. Ozel
I. Kaymaz
Y. Totik
机构：
[1] Ataturk University,Department of Mechanical Engineering, Faculty of Engineering
来源：
Journal of Materials Engineering and Performance | 2005年 / 14卷
关键词：
finite-element analysis; prestraining; residual stress; rotating bending fatigue;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The effect of tensile prestraining-induced residual stress on the fatigue life of notched steel parts was investigated. The study was performed on AISI 4140 steel. Rotating bending fatigue tests were carried out on semicircular notched specimens with different notch radii in the as-quenched and tempered conditions. Metallography of the specimens was performed by means of light optical microscopy. The finite-element method was used to evaluate the residual stress distribution near the notch region. Fatigue tests revealed fatigue life improvement for notched specimens, which changes depending on the notch radii and applied stress. Scanning electron microscopy was used to examine the fracture surfaces of the specimens.
引用
收藏
页码：351 / 355
页数：4
相关论文
共 50 条
  • [41] Calculation of fatigue limits of case-hardened specimens with consideration of mean stresses and residual stresses
    Jablonski, F
    Kienzler, R
    COMPUTATIONAL MECHANICS, 2002, 28 (05) : 401 - 405
  • [42] FATIGUE CRACK INITIATION IN NOTCHED SPECIMENS
    JACK, AR
    SCRIPTA METALLURGICA, 1971, 5 (08): : 721 - &
  • [43] Effect of residual stresses on fatigue crack initiation life for butt-welded joints
    Teng, TL
    Chang, PH
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 145 (03) : 325 - 335
  • [44] The effect of surface damage and residual stresses on the fatigue life of nickel superalloys at high temperature
    Fleury, R. M. N.
    Salvati, E.
    Nowell, D.
    Korsunsky, A. M.
    Silva, F.
    Tai, Y. H.
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 119 : 34 - 42
  • [45] Effect of edge distance ratio on residual stresses induced by cold expansion and fatigue life of TC4 plates
    Liu, Jun
    Wu, Henggui
    Yang, Jinjie
    Yue, Zhufeng
    ENGINEERING FRACTURE MECHANICS, 2013, 109 : 130 - 137
  • [46] Fatigue life predictions of notched specimens under non-proportional loadings
    Jin, Dan, 1600, Tsinghua University (31):
  • [47] NOTE ON RESIDUAL-STRESSES INDUCED BY FATIGUE CRACKING
    TIROSH, J
    LADELSKI, A
    ENGINEERING FRACTURE MECHANICS, 1980, 13 (03) : 453 - +
  • [48] Low Cycle Fatigue Life Evaluation of Notched Specimens Considering Strain Gradient
    Qin, Shenghuan
    Xiong, Zaiyin
    Ma, Yingsong
    Zhang, Keshi
    MATERIALS, 2020, 13 (04)
  • [49] FATIGUE LIFE PREDICTIONS OF SMOOTH AND NOTCHED SPECIMENS BASED ON FRACTURE-MECHANICS
    ELHADDAD, MH
    TOPPER, TH
    TOPPER, TN
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1981, 103 (02): : 91 - 96
  • [50] The study on the influences of residual stresses on fatigue crack propagation in titanium alloy specimens
    Zangeneh, A.
    Sattarifar, I.
    Noghabi, M.
    JOURNAL OF MECHANICAL ENGINEERING AND SCIENCES, 2022, 16 (04) : 9187 - 9196
12345