Measuring the complex modulus of polymers by instrumented indentation testing

被引：0
|
作者：
J. Hay
E. Herbert
机构：
[1] Agilent Technologies,Nanotechnology Measurements Operation
[2] University of Tennessee,Department of Material Science and Engineering
来源：
Experimental Techniques | 2013年 / 37卷
关键词：
Dynamic Testing; Elasticity; Damping; Instrumented Indentation; Nanoindentation; Time-Dependent Materials; Viscoelasticity;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Instrumented indentation is used to measure the complex modulus of highly plasticized polyvinyl chloride (HP-PVC) and four kinds of polyethylene over the frequency range of 1–50Hz. Over this range, the loss factor for the HP-PVC increases from 0.3 to 1, making this an ideal material for damping out noise and vibration. The storage moduli for the four polyethylene samples are ordered according to density, with the lowest-density material have the lowest storage modulus. Results for both storage modulus and loss factor compare well with published results obtained by dynamic mechanical analysis for nominally similar materials.
引用
收藏
页码：55 / 61
页数：6
相关论文
共 50 条
  • [21] Towards a reliable procedure for the measurement of elastic modulus in instrumented indentation
    Alkorta, Jon
    Martinez-Esnaola, Jose M.
    Gil Sevillano, Javier
    [J]. PHILOSOPHICAL MAGAZINE, 2011, 91 (7-9) : 1400 - 1408
  • [22] Effect of the Scale Factor on the Elastic Modulus Determined by Instrumented Indentation
    V. M. Matyunin
    A. Yu. Marchenkov
    P. V. Volkov
    M. A. Karimbekov
    A. A. Pan’kina
    [J]. Russian Metallurgy (Metally), 2023, 2023 : 2113 - 2119
  • [23] Instrumented indentation testing: A draft ASTM practice
    Tobolski, Ed
    [J]. Standardization News, 2003, 31 (10) : 34 - 37
  • [24] Instrumented indentation testing in materials research and development
    Jennett, Nigel M.
    Pharr, George M.
    McHargue, Carl J.
    [J]. PHILOSOPHICAL MAGAZINE, 2006, 86 (33-35) : 5153 - 5154
  • [25] A method for measuring the contact area in instrumented indentation testing by tip scanning probe microscopy imaging
    Charleux, L.
    Keryvin, V.
    Nivard, M.
    Guin, J. -P.
    Sangleboeuf, J. -C.
    Yokoyama, Y.
    [J]. ACTA MATERIALIA, 2014, 70 : 249 - 258
  • [26] Viscoelastic characterization of polymers using dynamic instrumented indentation
    White, CC
    Drzal, PL
    VanLandingham, MR
    [J]. FUNDAMENTALS OF NANOINDENTATION AND NANOTRIBOLOGY III, 2005, 841 : 187 - 192
  • [27] Martens hardness, indentation hardness or indentation modulus are determined - Instrumented indentation test according to ISO/DIS 14577
    Ullner, C.
    Wehrstedt, A.
    [J]. HTM - Haerterei-Technische Mitteilungen, 2001, 56 (04): : 242 - 248
  • [28] Measuring the complex modulus of asphalt concrete using ultrasonic testing
    Van Velsor, J.K.
    Premkumar, L.
    Chehab, G.
    Rose, J.L.
    [J]. Journal of Engineering Science and Technology Review, 2011, 4 (02) : 160 - 168
  • [29] An Instrumented Indentation Method for Young's Modulus Measurement with Accuracy Estimation
    Ma, D.
    Ong, C. W.
    Zhang, T.
    [J]. EXPERIMENTAL MECHANICS, 2009, 49 (05) : 719 - 729
  • [30] An Instrumented Indentation Method for Young’s Modulus Measurement with Accuracy Estimation
    D. Ma
    C. W. Ong
    T. Zhang
    [J]. Experimental Mechanics, 2009, 49 : 719 - 729
12345