Preparation, characterization and thermal behavior of poly(vinyl alcohol)/organic montmorillonite nanocomposites through solid-state shear pan-milling

In this study, the solid-state shear pan-milling was employed to prepare a series of polymer/layered silicate (PLS) nanocomposites. During the process of pan-milling at ambient temperature, poly(vinyl alcohol)/organic montmorillonite (PVA/OMMT) can be effectively pulverized, resulting in coexistence of intercalated and exfoliated OMMT layers. The obtained PLS nanocomposites were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). TEM analysis indicated that OMMT dispersed homogeneously in PVA matrix and XRD results illustrated that pan-milling had an obvious effect on increase in the interlayer spacing of OMMT, and resulted in coexistence of intercalated and exfoliated OMMT layers formed. Thermal gravimetric analysis showed that thermal stability of PVA was improved owing to the incorporation of OMMT. Thermal decomposition kinetics of PVA/OMMT nanocomposites with different milling cycles of OMMT was also studied. Two types of OMMT are chosen to compare the effect of hydrophilicity of OMMT on PVA/OMMT nanocomposites.