Effect of High Strain Rate on Low-Cycle Fatigue Behavior of Steel Welded Joints During Earthquake Loading

被引：0
|
作者：
N. Sinsamutpadung
E. Sasaki
机构：
[1] Tokyo Institute of Technology,Department of Civil Engineering
来源：
International Journal of Steel Structures | 2018年 / 18卷
关键词：
Low-cycle fatigue; High strain rate; Steel welded joint; Earthquake loading;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This study aims to investigate the effects of strain rate on the low-cycle fatigue strength of steel welded joints. Load-carrying cruciform joints with different material mismatch ratios were fabricated in order to observe the effects of material mismatching. A series of displacements that generate low-cycle fatigue damage were applied to the specimens. The experiment was conducted by fast cyclic loading and displacement control, using feedback from a displacement transducer. The feedback control algorithm was found to be critical. Thus, a non-linear feedback control algorithm, i.e., PID control, was implemented in the testing machine. An experimental setup capable of fast cyclic loading was developed. Fatigue life based on the load drop curve indicated that higher strain rates caused lower fatigue life. Failure behavior regarding the strain rate effects of steel welded joints was observed.
引用
收藏
页码：793 / 801
页数：8
相关论文
共 50 条
  • [1] Effect of High Strain Rate on Low-Cycle Fatigue Behavior of Steel Welded Joints During Earthquake Loading
    Sinsamutpadung, N.
    Sasaki, E.
    INTERNATIONAL JOURNAL OF STEEL STRUCTURES, 2018, 18 (03) : 793 - 801
  • [2] LOW-CYCLE FATIGUE OF AUSTENITIC STEEL STEAMLINES WITH WELDED JOINTS
    RATNER, AV
    PLOTNIKO.VP
    THERMAL ENGINEERING, 1968, 15 (07) : 10 - &
  • [3] RESIDUAL STRESS AND STRAIN RESPONSES OF WELDED PIPING JOINTS UNDER LOW-CYCLE FATIGUE LOADING
    Cheng, Pei-Yuan
    Hassan, Tasnim
    ASME PRESSURE VESSELS AND PIPING CONFERENCE 2009, VOL 1: CODES AND STANDARDS, 2010, : 95 - 101
  • [4] Low-cycle fatigue behavior of differently matched welded joints of quenched and tempered steel
    Gaspar, M.
    Dobosy, A.
    Meilinger, A.
    Nagy, Gy.
    WELDING IN THE WORLD, 2023, 67 (09) : 2247 - 2259
  • [5] Low-cycle fatigue behavior of differently matched welded joints of quenched and tempered steel
    M. Gáspár
    Á. Dobosy
    Á. Meilinger
    Gy. Nagy
    Welding in the World, 2023, 67 : 2247 - 2259
  • [6] PROPERTIES OF WELDED-JOINTS IN THE CONDITIONS OF STRAIN AGING DURING LOW-CYCLE LOADING
    DAUNIS, MA
    DAUNENE, SA
    TIMOFEEV, BT
    WELDING PRODUCTION, 1983, 29 (12): : 10 - 13
  • [7] PROPERTIES OF WELDED JOINTS IN THE CONDITIONS OF STRAIN AGEING DURING LOW-CYCLE LOADING.
    Daunis, M.A.
    Daunene, S.A.
    Timofeev, B.T.
    Welding Production (English translation of Svarochnoe Proizvodstvo), 1982, 29 (12): : 10 - 13
  • [8] LOW-CYCLE FATIGUE OF WELDED JOINTS.
    Rie, Kyong-Tschong
    Schmidt, Ralph-Michael
    Schweissen und Schneiden/Welding and Cutting, 1986, 38 (10):
  • [9] Effect of Static Loading Component on Low-Cycle Fatigue of Austenite-Class Steel and Its Welded Joints.
    Giginyak, F.F.
    Bashta, V.V.
    Ulin, V.P.
    Timofeev, B.T.
    Mozharovskaya, T.N.
    Problemy Prochnosti, 1985, (07): : 50 - 55
  • [10] Effect of Loading Rate on Low-Cycle Fatigue Properties of Turbine Rotor Steel
    He, Jianjun
    Chen, Jian
    Sun, Qingmin
    20TH EUROPEAN CONFERENCE ON FRACTURE, 2014, 3 : 1773 - 1779
12345