Mechanochemical processing of nanocrystalline Ti-6Al-4V alloy

被引：0
|
作者：
M. D. S. Pirzada
F. H. (Sam) Froes
S. N. Patankar
机构：
[1] the University of Idaho,Department of Materials and Metallurgical Engineering
[2] the University of Idaho,Institute for Materials and Advanced Processes
来源：
Metallurgical and Materials Transactions A | 2004年 / 35卷
关键词：
Milling; Material Transaction; Dehydrogenation; Powder Mixture; Ignition Time;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Synthesis of nanocrystalline Ti-6Al-4V was explored using mechanochemical processing. The reaction mixture was comprised of CaH2, Mg powder, anhydrous AlCl3, anhydrous VCl3, and TiCl4. The milled powder (reaction product) primarily consisted of nanocrystalline alloy hydride having a composition (Ti-6Al-4V)H1.942, along with MgCl2 and CaCl2 as by-products. Aqueous solutions of nitric acid, sulfuric acid, and 1 pct sodium sulfite were found to be very effective in leaching of the chlorides from the milled powder. The (Ti-6Al-4V)H1.942 on dehydrogenation at 375°C resulted in nanocrystalline Ti-6Al-4V alloy powder.
引用
收藏
页码：1899 / 1903
页数：4
相关论文
共 50 条
  • [31] Dehydrogenation of hydrogenated Ti-6Al-4V alloy
    Yuan, Baoguo, 1600, Science Press (43):
  • [32] MICRODUPLEX STRUCTURE IN THE TI-6AL-4V ALLOY
    VIJAYAKAR, SJ
    BANERJEE, S
    KRISHNAN, R
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1978, 31 (5-6): : 302 - &
  • [33] HOT WORKABILITY OF A TI-6AL-4V ALLOY
    FUJII, H
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 (05): : S751 - S751
  • [34] Structural transformations in Ti-6Al-4V alloy
    Tarin, P.
    Gil, F.X.
    Ginebra, M.P.
    Manero, J.M.
    Prado, J.M.
    Sole, M.
    Planell, J.A.
    Journal De Physique, 1995, 5 (02) : 2 - 317
  • [35] Damage mechanisms of torsion-tested Ti-6Al-4V alloy and TiCp/Ti-6Al-4V composite
    Zhu, JH
    Liaw, PK
    Corum, JM
    Ruggles, MB
    JOHANNES WEERTMAN SYMPOSIUM, 1996, : 127 - 134
  • [36] High-temperature mechanical behavior of Ti-6Al-4V alloy and TiCp/Ti-6Al-4V composite
    J. H. Zhu
    P. K. Liaw
    J. M. Corum
    H. E. McCoy
    Metallurgical and Materials Transactions A, 1999, 30 : 1569 - 1578
  • [37] Machinability of cast Ti and Ti-6Al-4V alloy.
    Watanabe, I
    Ford, JP
    Nakajima, H
    Hosoi, T
    Okabe, T
    JOURNAL OF DENTAL RESEARCH, 1998, 77 : 165 - 165
  • [38] Deformation mechanisms of nanocrystalline alpha titanium in Ti-6Al-4V
    Liu, Y. G.
    Li, M. Q.
    MATERIALS LETTERS, 2016, 185 : 488 - 490
  • [39] DIFFUSION BONDING OF SIC/TI-6AL-4V COMPOSITE TO TI-6AL-4V ALLOY AND FRACTURE-BEHAVIOR OF JOINT
    FUKUMOTO, S
    HIROSE, A
    KOBAYASHI, KF
    MATERIALS SCIENCE AND TECHNOLOGY, 1993, 9 (06) : 520 - 527
  • [40] Diffusion bonding of TiC or TiB reinforced Ti-6Al-4V matrix composites to conventional Ti-6Al-4V alloy
    Prikhodko, Sergey, V
    Savvakin, Dmytro G.
    Markovsky, Pavlo E.
    Stasuk, Olexander O.
    Penney, James
    Shirzadi, Amir A.
    Davies, Peter D.
    Davies, Helen M.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2020, 25 (06) : 518 - 524
12345