Prerequisites for high-quality magnetic tunnel junctions: XPS and NMR study of Co/Al bilayers

Aluminum films with thicknesses ranging from 1 nm to 12 nm have been sputtered on 20 nm thick Co layers. The properties of the Co/Al bilayers were studied by X-ray photoemission spectroscopy (XPS) and spin-echo nuclear magnetic resonance (NMR). Both methods show independently that a 1 nm Al film covers the Co surface completely. XPS and NMR also showed that layers thicker than 1 nm Al are not oxidized completely in ambient air. Similarities to and deviations from niobium with Al overlayers (Nb/Al) are described. Prerequisites for the fabrication of tunneling magnetoresistance devices based on Co or NiFe ferromagnets and an aluminum oxide barrier are discussed.