Single solid-oxide fuel cells with supporting ni-cermet anode

Single solid-oxide fuel cells (SOFCs) with a porous (36-41%) supporting Ni-cermet anode are manufactured and tested. The effect of the thickness of the supporting Ni-cermet anode on the electrochemical characteristics of single SOFCs is studied. It is shown that polarization losses on electrodes at the current density of 1.2 A/cm2 increase by about 2 times from 0.13 to 0.25 V at an increase in the thickness of the supporting Ni-cermet anode from 0.40 to 1.27 mm. The impedance spectroscopy method is used to identify relaxation processes responsible for the behavior of the fuel cell anode and cathode. It is found that a significant percentage of polarization losses on the anode is due to transport limitations in fuel supply to the three-phase nickel/electrolyte/gas phase interface and removal of the reaction products away from it.