Structure and Properties of Welded Joints of High-Strength Steels Made by Metal-Cored Wire with Nitrogen

被引：0
|
作者：
A. S. Smolentsev
V. E. Veselova
A. V. Berezovsky
E. A. Usoltsev
A. V. Shak
机构：
[1] Ural Federal University named after first President of Russia B. N. Yeltsin,Institute of Engineering Science
[2] UB RAS,undefined
来源：
Metallurgist | 2024年 / 67卷
关键词：
arc welding; high-strength steels; hull structures; special equipment; metal-cored wire; nitrogen; austenite;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
An austenitic metal-cored wire (diameter – 1.6 mm) with additional nitrogen alloying (0.25–0.40 wt.%) was developed for this study. Mechanical tests and metallographic studies of the deposited metal and welded joints made with austenitic metal-cored wire (composition – Cr20Mn5Ni4Mo2.5Cu3N0.3) were conducted. It was found that the values of σu and σ0.2 of the deposited metal obtained by using the developed wire were 20 to 30% higher compared to the utilized electrode materials, while the ductility characteristics were preserved (δ = 43%). It was shown that the use of metal-cored wire (Cr20Mn5Ni4Mo2.5Cu3N0.3) for welding of high-strength steel 20HGSNM (EN 1.6523) makes it possible to obtain defect-free welded joints with austenitic-ferritic structure, which have 20% higher strength characteristics compared to the analogues.
引用
收藏
页码：1334 / 1343
页数：9
相关论文
共 50 条
  • [21] Welding of S1100 Ultra high-Strength Steel Plates with Matching Metal-Cored Filler Wire: Microstructure, Residual Stresses, and Mechanical Properties
    Tumer, Mustafa
    Pixner, Florian
    Vallant, Rudolf
    Warchomicka, Fernando Gustavo
    Domitner, Josef
    Enzinger, Norbert
    STEEL RESEARCH INTERNATIONAL, 2024, 95 (05)
  • [22] Microstructural and mechanical characterization of welded joints on innovative high-strength steels
    Holovenko, O.
    Lenco, M. G.
    Pastore, E.
    Pinasco, M. R.
    Matteis, P.
    Scavino, G.
    Firrao, D.
    METALLURGIA ITALIANA, 2013, (03): : 3 - 12
  • [23] DISSIMILAR HIGH-STRENGTH STEELS: FUSION WELDED JOINTS, MISMATCHES, AND CHALLENGES
    Mvola, B.
    Kah, P.
    Martikainen, J.
    Suoranta, R.
    REVIEWS ON ADVANCED MATERIALS SCIENCE, 2016, 44 (02) : 146 - 159
  • [24] METHODS OF IMPROVING DUCTILITY OF WELDED-JOINTS IN HIGH-STRENGTH STEELS
    SAVCHENKO, VA
    SOTNIK, IS
    AUTOMATIC WELDING USSR, 1973, 26 (06): : 75 - 77
  • [25] CAPACITY OF FILLET WELDED JOINTS MADE OF ULTRA HIGH-STRENGTH STEEL
    Bjork, T.
    Toivonen, J.
    Nykanen, T.
    WELDING IN THE WORLD, 2012, 56 (3-4) : 71 - 84
  • [26] Effect of the Morphology of Structure on the Resistance of Welded Joints of High-Strength Pipe Steels to Brittle Fracture
    Efimenko, L. A.
    Ramus', A. A.
    METAL SCIENCE AND HEAT TREATMENT, 2016, 57 (9-10) : 559 - 563
  • [27] Capacity of Fillet Welded Joints Made of Ultra High-Strength Steel
    Timo Björk
    Joe Toivonen
    Timo Nykänen
    Welding in the World, 2012, 56 : 71 - 84
  • [28] ECONOMIC STIMULATION OF PRODUCTION OF WELDED PRODUCTS MADE OF HIGH-STRENGTH STEELS
    PANASHCH.NI
    KHARCHEN.PF
    AUTOMATIC WELDING USSR, 1972, 25 (06): : 52 - &
  • [29] Effect of the Morphology of Structure on the Resistance of Welded Joints of High-Strength Pipe Steels to Brittle Fracture
    L. A. Efimenko
    A. A. Ramus’
    Metal Science and Heat Treatment, 2016, 57 : 559 - 563
  • [30] SPOT-WELDING OF HIGH-STRENGTH STEELS FOR DEEP DRAWING AND PROPERTIES OF THE WELDED-JOINTS
    DEFOURNY, J
    DHAEYER, R
    BRAGARD, A
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 1982, 79 (06): : 531 - 544
12345