Influence of Ti addition on the hydrogen induced cracking of API 5L X70 hot-rolled pipeline steel in acid sour media

被引：0
|
作者：
Joonoh Moon
Chulbong Park
Seong-Ju Kim
机构：
[1] Korea Institute of Materials Science,Ferrous Alloy Department, Advanced Metallic Materials Division
[2] Hyundai Steel Company,Sheet Products Design Team, Technical Research Center
来源：
Metals and Materials International | 2012年 / 18卷
关键词：
metals; rolling; corrosion; precipitation; hydrogen;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In this study, Hydrogen Induced Cracking (HIC) testing of high strength API 5L grade X70 linepipe hot rolled steel containing Ti was performed to investigate the effects of (Nb, Ti, V)(C, N) particles on HIC susceptibility. By controlling chemical composition and hot rolling parameters, experimental steel with Bainitic ferrite and Bainite microstructures was fabricated. HIC testing was carried out within an acidic condition (pH=2.7±0.1) according to NACE standards with test results showing cracking propagated along coarse (Nb, Ti, V)(C, N) particles at mid-thickness. This is mainly due to centerline segregation and hydrogen blistering between matrix and coarse (Nb, Ti, V)(C, N) particles without external stress.
引用
收藏
页码：613 / 617
页数：4
相关论文
共 50 条
  • [21] INVESTIGATION INTO COLD CRACKING IN UNDERWATER WET WELDING OF API 5L X70 STEEL
    Garasic, Ivica
    Kralj, Slobodan
    Kozuh, Zoran
    TRANSACTIONS OF FAMENA, 2009, 33 (03) : 25 - 34
  • [22] Hydrogen Cracking in an API 5L X70 Steel Welded with Cellulosic Electrodes of Different Levels of Mechanical Resistance
    Mattioli, Camila Goes
    Modenesi, Paulo Jose
    Bracarense, Alexandre Queiroz
    Oliveira, Matheus Pires
    SOLDAGEM & INSPECAO, 2018, 23 (01): : 113 - 125
  • [23] Effect of Different Microstructural Parameters on Hydrogen Induced Cracking in an API X70 Pipeline Steel
    Mohtadi-Bonab, M. A.
    Eskandari, M.
    Karimdadashi, R.
    Szpunar, J. A.
    METALS AND MATERIALS INTERNATIONAL, 2017, 23 (04) : 726 - 735
  • [24] Effect of different microstructural parameters on hydrogen induced cracking in an API X70 pipeline steel
    M. A. Mohtadi-Bonab
    M. Eskandari
    R. Karimdadashi
    J. A. Szpunar
    Metals and Materials International, 2017, 23 : 726 - 735
  • [25] The effect of hydrogen and notch orientation in SENT specimens on the fracture toughness of an API 5L X70 pipeline steel
    Depraetere, Robin
    De Waele, Wim
    Cauwels, Margo
    Depover, Tom
    Verbeken, Kim
    Hertele, Stijn
    ENGINEERING FRACTURE MECHANICS, 2024, 300
  • [26] Corrosion Inhibition Efficiency of Ghars Date Extract on API 5L X70 Pipeline Steel in Hydrochloric Acid
    Slimane Kherief
    Mounir Djellab
    Hamza Bentrah
    Abdelouahad Chala
    Bouzid Bouamra
    Hicham Taoui
    Protection of Metals and Physical Chemistry of Surfaces, 2023, 59 : 1306 - 1314
  • [27] Slab cracking after continuous casting of API 5L X-70 grade steel for pipeline sour gas application
    Mendoza, R
    Huante, J
    Alanis, M
    Gonzalez-Rivera, C
    Juarez-Islas, JA
    IRONMAKING & STEELMAKING, 1999, 26 (03) : 205 - 209
  • [28] Slab cracking after continuous casting of API 5L X-70 grade steel for pipeline sour gas application
    Mendoza, R.
    Huante, J.
    Alanis, M.
    Gonzalez-Rivera, C.
    Juarez-Islas, J.A.
    Ironmaking and Steelmaking, 1999, 26 (03): : 205 - 209
  • [29] Corrosion Inhibition Efficiency of Ghars Date Extract on API 5L X70 Pipeline Steel in Hydrochloric Acid
    Kherief, Slimane
    Djellab, Mounir
    Bentrah, Hamza
    Chala, Abdelouahad
    Bouamra, Bouzid
    Taoui, Hicham
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2023, 59 (06) : 1306 - 1314
  • [30] Effect of Microstructure and Texture Evolution on the Electrochemical Corrosion Behavior of Warm-Rolled API 5L X70 Pipeline Steel
    Ohaeri, Enyinnaya
    Omale, Joseph
    Eduok, Ubong
    Szpunar, Jerzy
    Arafin, Muhammad
    Fazeli, Fateh
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2020, 51 (05): : 2255 - 2275
12345