Effect of Solidification Rate and Heat Treating on the Microstructure and Tensile Behavior of an Aluminum-Copper Alloy

被引:0
|
作者
M.A. Talamantes-Silva
A. Rodríguez
J. Talamantes-Silva
S. Valtierra
R. Colás
机构
[1] Universidad Autónoma de Nuevo León,Facultad de Ingeniería Mecánica y Eléctrica
[2] University of Sheffield,Department of Engineering Materials
[3] Nemak,undefined
[4] S.A. de C.V.,undefined
[5] Owens Corning,undefined
[6] Privada la Puerta 1110-A,undefined
[7] Parque Industrial La Puerta,undefined
关键词
Solidification Rate; Microstructural Refining; Average Cool Rate; Solidification Kinetic; Metallographic Plane;
D O I
暂无
中图分类号
学科分类号
摘要
An aluminum-copper alloy of the A206 type was melt and cast in molds that promote a thermal gradient during solidification to study the effects that solidification rate exerts on the microstructure of the material. The stress-strain characteristics of heat-treated samples were related to microstructural parameters. The reactions occurring during solidification and cooling were detected and identified by means of thermal analyses. The microstructure of the material was assessed by measuring the secondary dendrite arm spacing, grain size, and porosity. It was found that these parameters increase as the solidification rate decreases. The material was heat treated to T4 and T7 conditions and tested in tension. The stress-strain curves were analyzed to determine the yield and ultimate strengths, as well as the strain to failure and that at which the ultimate strength was achieved. It was found that these properties are enhanced by microstructural refining in either testing condition. It was also found that porosity increased due to dissolution of copper-rich particles during heat treating. The best combination of strength and ductility were achieved in the T4 condition.
引用
收藏
页码:911 / 919
页数:8
相关论文
共 50 条
  • [31] Effect of Weld Parameters on the Microstructure of Aluminum-Copper Joints Produced by Flash Welding
    A. Shafiei
    V. Yerevanian
    D. M. Maijer
    [J]. Journal of Materials Engineering and Performance, 2020, 29 : 5214 - 5226
  • [32] LOSS OF COHERENCY OF THETA' PRECIPITATES IN AN ALUMINUM-COPPER ALLOY
    NEMOTO, M
    OGUCHI, T
    MORISHIG.N
    SUTO, H
    [J]. TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1971, 12 (06): : 429 - &
  • [33] MICROSTRUCTURAL CHANGES IN AN ALUMINUM-COPPER ALLOY DURING WELDING
    DUMOLI, S
    LAUGHLIN, DE
    WILLIAMS, JC
    [J]. JOURNAL OF METALS, 1980, 32 (08): : 80 - 80
  • [34] EFFECT OF LORENTZ FORCE ON THE SOLIDIFICATION STRUCTURE OF ALUMINUM - COPPER ALLOY
    AMBARDAR, R
    SHARMA, DGR
    PRABHAKAR, O
    [J]. TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1994, 47 (2-3): : 131 - 137
  • [35] CASTABILITY TESTS APPLIED TO ALL ALUMINUM-COPPER ALLOY
    GARDA, B
    FORTIN, L
    DURAND, F
    [J]. JOURNAL DE PHYSIQUE IV, 1993, 3 (C7): : 239 - 242
  • [36] Implementation of specifically designed deep neural networks for the prediction and optimization of tensile properties of aluminum-copper alloy
    Nikzad, Mohammad Hossein
    Heidari-Rarani, Mohammad
    Momenzadeh-Kholenjani, Ali
    Rasti, Reza
    [J]. MATERIALS TODAY COMMUNICATIONS, 2024, 39
  • [37] DISLOCATION DAMPING AT HIGH STRAIN RATES IN ALUMINUM AND ALUMINUM-COPPER ALLOY
    VICTORIA, MP
    DHARAN, CKH
    HAUSER, FE
    DORN, JE
    [J]. JOURNAL OF APPLIED PHYSICS, 1970, 41 (02) : 674 - &
  • [38] EFFECT OF SOLIDIFICATION MICROSTRUCTURE ON CORROSION BEHAVIOR OF A GRAIN-REFINED ALUMINIUM-COPPER ALLOY
    MURTY, YVVRS
    KATTAMIS, TZ
    DEVEREUX, OF
    [J]. JOURNAL OF MATERIALS SCIENCE, 1974, 9 (04) : 688 - 692
  • [39] Age-hardening of aluminum alloys, I - Aluminum-copper alloy
    Fink, WL
    Smith, DW
    [J]. TRANSACTIONS OF THE AMERICAN INSTITUTE OF MINING AND METALLURGICAL ENGINEERS, 1936, 122 : 284 - 293
  • [40] Effect of Plug Materials on Microstructure and Tensile Fracture Behavior of Aluminum Alloy Friction Plug Welds
    Du Bo
    Yang Xin-qi
    Sun Zhuan-ping
    Wang Dong-po
    [J]. CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2018, 46 (12): : 137 - 143