Research in the Area of Preparing Materials Based on Fuzed Quartz HCBS. Part 2. Quartz Steel-Pouring Refractories1

被引：0

作者：

Yu. E. Pivinskii

机构：

[1] OOO NVF Kerambet-Ogneupor,

来源：

Refractories and Industrial Ceramics | 2015年 / 56卷

关键词：

fuzed quartz; quartz steel-pouring refractories; CBCM; corundum-graphite refractories; centrifugal molding; HCBS; ceramic concrete;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Comparative evaluation is given for production and application of contemporary quartz steel-pouring ladle refractories for OAO Dinur CBCM production with similar corundum-graphite refractories produced in the Russian Federation by overseas technology using imported equipment. In spite of numerous predictions the actual 45-year practice of continuous improvement of quartz refractories demonstrates their good viability. Good technical and economic efficiency of their production and application is achieved by implementation of HCBS- and ceramic concrete technology with application of unique centrifugal molding used for the first time on an extensive industrial scale.

引用

页码：20 / 25

页数：5

共 50 条

[41] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 3. Effect of Firing Temperature on Sintering and Mullitization of Materials Prepared on the Basis of Composite Composition HCBS1
Pivinskii, Yu. E.
Dyakin, P. V.
Ostryakov, L. V.
REFRACTORIES AND INDUSTRIAL CERAMICS, 2016, 56 (06) : 648 - 655
[42] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 3. Effect of Firing Temperature on Sintering and Mullitization of Materials Prepared on the Basis of Composite Composition HCBS1
Yu. E. Pivinskii
P. V. Dyakin
L. V. Ostryakov
Refractories and Industrial Ceramics, 2016, 56 : 648 - 655
[43] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 5. Effect of Firing Temperature on Properties of Materials Prepared From Composite HCBS With Addition of Refractory Clay1
Yu. E. Pivinskii
P. V. Dyakin
L. V. Ostryakov
Refractories and Industrial Ceramics, 2016, 57 : 180 - 184
[44] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 7. Sintering and Secondary Mullite Formation of Materials Based on Composite Composition HCBS During Nonisothermal Heating and Isothermal Firing1
Yu. E. Pivinskii
P. V. Dyakin
Refractories and Industrial Ceramics, 2017, 57 : 536 - 544
[45] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 5. Effect of Firing Temperature on Properties of Materials Prepared From Composite HCBS With Addition of Refractory Clay1
Pivinskii, Yu. E.
Dyakin, P. V.
Ostryakov, L. V.
REFRACTORIES AND INDUSTRIAL CERAMICS, 2016, 57 (02) : 180 - 184
[46] RESEARCH IN THE FIELD OF PREPARING MOLDED AND UNMOLDED REFRACTORIES BASED ON HIGH-ALUMINA HCBS. PART 7. SINTERING AND SECONDARY MULLITE FORMATION OF MATERIALS BASED ON COMPOSITE COMPOSITION HCBS DURING NONISOTHERMAL HEATING AND ISOTHERMAL FIRING
Pivinskii, Yu. E.
Dyakin, P. V.
REFRACTORIES AND INDUSTRIAL CERAMICS, 2017, 57 (05) : 536 - 544
[47] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 1. High-Alumina Bauxite as a Basic Raw Material Component
Pivinskii, Yu. E.
Dyakin, P. V.
Perepelitsyn, V. A.
REFRACTORIES AND INDUSTRIAL CERAMICS, 2015, 56 (04) : 344 - 350
[48] Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 1. High-Alumina Bauxite as a Basic Raw Material Component
Yu. E. Pivinskii
P. V. Dyakin
V. A. Perepelitsyn
Refractories and Industrial Ceramics, 2015, 56 : 344 - 350
[49] Production Process And Service Of Quartz Steel-Casting Refractories. Part 2. 1 Some Properties And Special Features Of Service
E. M. Grishpun
Yu. E. Pivinskii
E. V. Rozhkov
Refractories and Industrial Ceramics, 1999, 40 : 268 - 272
[50] Production process and service of quartz steel-casting refractories. Part 2. Some properties and special features of service
Grishpun, EM
Pivinskii, YE
Rozhkov, EV
REFRACTORIES AND INDUSTRIAL CERAMICS, 1999, 40 (5-6) : 268 - 272

← 1 2 3 4 5 →