Effect of additives on the firing temperature of a current-conducting composite

被引：0
|
作者：
S. P. Rodtsevich
G. G. Mamedova
机构：
[1] Academy of Sciences of Belarus,Institute of General and Inorganic Chemistry
来源：
Glass and Ceramics | 1997年 / 54卷
关键词：
Uric Acid; Precious Metal; Firing Temperature; Heating Element; Indium Oxide;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A study was undertaken to see how sulfuric acid and alkalis would affect the firing temperature of a current-conducting composite. It was found that sulfuric acid, when added to the composite, acts to depress the firing temperature, and the alkali causes it to rise. The proposed current-conducting coatings will extend the service life of heating elements, improve their efficiency, and exclude the use of the precious metals.
引用
收藏
页码：96 / 97
页数：1
相关论文
共 50 条
  • [11] Current-conducting adhesives developed at OAO Kompozit
    Gladkikh S.N.
    Kuznetsova L.I.
    Kornev V.V.
    Barkovskaya N.P.
    Polymer Science - Series D, 2009, 2 (04) : 243 - 245
  • [12] Effect of additives on firing temperature of conductive composition
    Inst Obshchej i Neorganicheskoj, Khimii AN Belarusi, Minsk, Belarus
    Steklo i Keramika, 1997, (03): : 27 - 28
  • [13] SHAPE OF CURRENT-CONDUCTING CHANNEL IN ARC COLUMN
    ZARUBA, II
    AUTOMATIC WELDING USSR, 1967, 20 (11): : 23 - &
  • [14] PRODUCTION OF PERICLASE IN A FURNACE WITH A CURRENT-CONDUCTING BOTTOM
    AVTUKHOV, VV
    MECHEV, VV
    TIKHONOV, VP
    SKORODUMOV, VV
    CHETYRKIN, AL
    STRIZHKO, VS
    SMIRNOVA, RI
    REFRACTORIES, 1984, 25 (1-2): : 96 - 98
  • [15] CHEMICOTHERMAL TREATMENT IN CURRENT-CONDUCTING POWDERED MIXTURES
    PROSVIRIN, VI
    GERASIMOV, LV
    TARASOV, VA
    METAL SCIENCE AND HEAT TREATMENT, 1978, 20 (9-10) : 759 - 761
  • [16] Formation of current-conducting surface layer on piezoceramics
    Solov'ev, L.A.
    Lobas, L.M.
    Lupejko, T.G.
    Karimova, L.A.
    Steklo i Keramika, 1991, (10): : 19 - 20
  • [17] Current-conducting coatings from aluminum powder compositions
    E. V. Shinkareva
    V. V. Tavgen’
    Glass and Ceramics, 1997, 54 : 129 - 131
  • [18] Electromagnetic contribution to gravitational mass of a current-conducting channel
    Meierovich, BE
    PHYSICAL REVIEW D, 2000, 61 (02)
  • [19] Current-conducting coatings from aluminum powder compositions
    Shinkareva, EV
    Tavgen, VV
    GLASS AND CERAMICS, 1997, 54 (3-4) : 129 - 131
  • [20] Electric conduction of current-conducting rubbers at low temperatures
    Kauch Rezina, 5 (26-27):
12345