Effect of Bi2O3 coating on interfacial wettability and tensile properties of Al18B4O33w/Al composite

被引：0
|
作者：
Z. J. Li
L. D. Wang
H. Y. Yue
W. D. Fei
机构：
[1] Harbin Institute of Technology,School of Materials Science and Engineering
来源：
Journal of Materials Science | 2007年 / 42卷
关键词：
Wettability; Ultimate Tensile Strength; Bi2O3; Interfacial Reaction; Squeeze Casting;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A pure aluminum matrix composite reinforced by Bi2O3-coated Al18B4O33 whisker was fabricated by squeeze casting method. The effects of Bi2O3 coating on the whisker/matrix wettability and the ultimate tensile strength and elongation to fracture of the composite are investigated. The results show that Bi2O3 coating can react with aluminum matrix during casting process, which improves the whisker/matrix wettability. Moreover, the ultimate tensile strength and elongation to fracture of the composite attain the maximum values at the mass ratio of 40:1 between whisker and Bi2O3 coating.
引用
收藏
页码：9355 / 9358
页数：3
相关论文
共 50 条
  • [31] Effects of whisker surface treatment on microstructures, tensile properties and aging behaviors of Al18B4O33w/6061Al composites
    Yue, H. Y.
    Song, S. S.
    Wang, B.
    Gao, X.
    Zhang, S. L.
    Yao, L. H.
    Lin, X. Y.
    Guan, E. H.
    Zhang, H. J.
    Guo, E. J.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 697 : 11 - 18
  • [32] Improvement in the corrosion resistance of Al18B4O33w/2024Al composite by laser surface treatment
    Hu, J.
    Liu, G.
    Li, Z. J.
    Kong, L. C.
    APPLIED SURFACE SCIENCE, 2007, 253 (10) : 4524 - 4530
  • [33] Effect of the aspect ratio of whisker on work hardening rate of as forged 2024Al/Al18B4O33w composite
    Yuan, Lin
    Shi, Wenchao
    Zheng, Zhenzhu
    Shan, Debin
    MATERIALS CHARACTERIZATION, 2015, 104 : 73 - 80
  • [34] Microstructure and electromagnetic properties of Al18B4O33w/CO composite particles prepared by electroless plating method
    Jiang, J. T.
    Zhen, L.
    Yang, L.
    Shao, W. Z.
    Xu, C. Y.
    Chao, Z. M.
    SURFACE & COATINGS TECHNOLOGY, 2009, 203 (16): : 2221 - 2228
  • [35] Controlling the interface reaction in Al18B4O33w/AC8A composite by nitrided nano-coating
    Bi, G
    Rao, QL
    Xi, F
    MATERIALS LETTERS, 2004, 58 (05) : 833 - 836
  • [36] Growth and microstructure of microarc oxidation coating on Al18B4O33w/AZ91 mg matrix composite
    Wu, K.
    Wang, Y. Q.
    Zheng, M. Y.
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 543 - +
  • [37] Effect of Extrusion Forming on Compressive Strength of Al18B4O33w/Mg Composites
    Li Zhengjia
    Li Hejun
    Qi Lehua
    Oy Haibo
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 : 41 - 44
  • [38] Hot deformation and processing maps of Al18B4O33w/ZK60 composite
    Wang, C. Y.
    Wu, K.
    Zheng, M. Y.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 477 (1-2): : 179 - 184
  • [39] Al18B4O33w/Bi/Al复合材料室温阻尼和力学性能
    刘刚
    胡津
    哈尔滨工业大学学报, 2012, 44 (05) : 92 - 96
  • [40] The effect of thermal exposure on the interface and mechanical properties of Al18B4O33w/AZ91 magnesium matrix composite
    Zheng, MY
    Wu, K
    Liang, A
    Kamado, S
    Kojima, Y
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 372 (1-2): : 66 - 74
12345