Waterborne epoxy resin modified by AMPS

被引：0
|
作者：
Chengyin Ma
Cuiyan Deng
Wenji Zheng
机构：
[1] Central South University,School of Chemistry and Chemical Engineering
来源：
Journal of Wuhan University of Technology-Mater. Sci. Ed. | 2007年 / 22卷
关键词：
waterborne epoxy resin; 2-acrylamido-2-methyl-1-propanesulfonic acid; grafting copolymerization; ring-opening polyaddition; soap-free emulsion;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A stable epoxy emulsion was prepared with epoxy resin (EP) as raw material, 2-acrylamido-2-methyl-1-propanesulfonic acid (AMPS) as modifier and benzoyl peroxide as initiator. By criterion of yield of the copolymer AMPS-EP, water-solubility, change of the acid value and intrinsic viscosity [η] along with reaction time, the copolymerization course was deduced. It is found that during the process, AMPS takes part in both the grafting copolymerization with epoxy principal chain and the ring-opening polyaddition with epoxy group. It is also discovered that the yield of AMPS-EP and water dispersing varies with reaction time. When it reaches 1.5 h, AMPS-EP can obtain good water-solubility; but the water-solubility will go bad gradually if it exceeds 3.5 h. IR spectrum analysis indicates that partial epoxy group partially remains and the others create sulfonic ester.
引用
收藏
页码：649 / 652
页数：3
相关论文
共 50 条
  • [21] Characterization and modelling of creep and recovery behaviour of waterborne epoxy resin modified bitumen emulsion
    Rui Li
    Zhen Leng
    Manfred N. Partl
    Christiane Raab
    Materials and Structures, 2021, 54
  • [22] Research on Curing Behavior and Performance of Waterborne Epoxy Resin Composite Modified Emulsified Asphalt
    Liu, Shengjie
    Cao, Xu
    Zhang, Yulin
    Fu, Yongteng
    Jiao, Xiaodong
    Cailiao Daobao/Materials Reports, 2024, 38 (24):
  • [23] Properties and mechanism of waterborne epoxy resin-SBR composite modified emulsified asphalt
    Liu, Fuqiang
    Zheng, Mulian
    Fan, Xianpeng
    Li, Hongyin
    Wang, Fei
    Lin, Xiaoyu
    CONSTRUCTION AND BUILDING MATERIALS, 2021, 274
  • [24] Sodium silicate/waterborne epoxy resin hybrid-modified Chinese fir wood
    Zhenyu Sun
    Jianxiong Lv
    Zhangheng Wang
    Yiqiang Wu
    Guangming Yuan
    Yingfeng Zuo
    Wood Science and Technology, 2021, 55 : 837 - 855
  • [25] Synthesis and properties of fumaropimaric acid-based waterborne polyurethane modified by epoxy resin
    Liu, He
    Xu, Xu
    Shang, Shi-Bin
    Song, Zhan-Qian
    Song, Zhan-Qian, 1600, Editorial Board of Chemistry and Industry of Forest Products (34): : 122 - 126
  • [26] Properties of new cold patch asphalt liquid and mixture modified with waterborne epoxy resin
    Zhang, Zhengqi
    Wang, Suqing
    Lu, Guodong
    INTERNATIONAL JOURNAL OF PAVEMENT ENGINEERING, 2020, 21 (13) : 1606 - 1616
  • [27] Compatibility evaluation between waterborne epoxy resin and SBR latex modified asphalt emulsion
    Yang, Jianhua
    Zhang, Zhengqi
    Fang, Ying
    JOURNAL OF TRAFFIC AND TRANSPORTATION ENGINEERING-ENGLISH EDITION, 2024, 11 (01) : 160 - 171
  • [28] Characterization and modelling of creep and recovery behaviour of waterborne epoxy resin modified bitumen emulsion
    Li, Rui
    Leng, Zhen
    Partl, Manfred N.
    Raab, Christiane
    MATERIALS AND STRUCTURES, 2021, 54 (01)
  • [29] Sodium silicate/waterborne epoxy resin hybrid-modified Chinese fir wood
    Sun, Zhenyu
    Lv, Jianxiong
    Wang, Zhangheng
    Wu, Yiqiang
    Yuan, Guangming
    Zuo, Yingfeng
    WOOD SCIENCE AND TECHNOLOGY, 2021, 55 (03) : 837 - 855
  • [30] Preparation and properties of self-matting waterborne polyurethane with silicon modified by epoxy resin
    Tang, Hui
    Yang, Jianjun
    Wu, Qingyun
    Wu, Mingyuan
    Zhang, Jian'an
    Liu, Jiuyi
    Jingxi Huagong/Fine Chemicals, 2020, 37 (10): : 2099 - 2104
12345