Corrosion-Fatigue Strength of Corrosion-Resistant Steels with Welded Joints

被引：0

作者：

M. S. Khoma

V. I. Pokhmurs'kyi

机构：

[1] Ukrainian Academy of Sciences,Karpenko Physicomechanical Institute

来源：

Materials Science | 2000年 / 36卷

关键词：

Fatigue; Welding; Stainless Steel; Plastic Deformation; Fatigue Crack;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

We consider the influence of argon-arc welding and the type of a weld on the corrosion-fatigue strength of specimens (d = 50 and 200 mm) made of 08Kh17N6T, 10Kh26N5M2, and 08Kh18G12N5AB stainless steels. We established that fatigue cracks are initiated from near-surface welding defects and fracture occurs along the weld. We showed that the use of surface plastic deformation is more efficient for enhancement of the corrosion-fatigue strength of welded specimens than cathodic protection.

引用

下载

页码：592 / 597

页数：5

共 50 条

[21] Surface Treatment of Welded Joints in Corrosion-Resistant Steels with 6% of Molybdenum and Nickel-Base Alloys
Rokel, M.
Herda, V.
Chemical and Petroleum Engineering, 1994, 30 (9-10)
[22] Corrosion of welded joints (III). Corrosion and its mitigation of welded joints in stainless steels
Matsushima, Iwao
Journal of the Japan Welding Society/Yosetsu Gakkai Shi, 1992, 61 (03):
[23] SPD INCREASES CORROSION-FATIGUE STRENGTH
NEMANOV, MS
RUSSIAN ENGINEERING JOURNAL-USSR, 1972, 52 (01): : 63 - &
[24] LOW MANGANESE CORROSION-RESISTANT STEELS
SZUMMER, A
LUBLINSKA, K
JANIKCZACHOR, M
ISIJ INTERNATIONAL, 1991, 31 (02) : 239 - 240
[25] THE USE OF CORROSION-RESISTANT STEELS FOR DIES
FASKHUTDINOV, RR
ZHURAVLEV, VN
NIKOLAEVA, OI
METAL SCIENCE AND HEAT TREATMENT, 1986, 28 (3-4) : 231 - 237
[26] CORROSION-RESISTANT MARAGING STEELS FOR MICROINSTRUMENTS
GELLER, YA
SEMICHESTNAYA, AV
PESETSKII, GM
LINNIK, VA
METAL SCIENCE AND HEAT TREATMENT, 1981, 23 (9-10) : 650 - 652
[27] STRESS CORROSION CRACKING OF WELDED JOINTS IN HIGH STRENGTH STEELS.
Gooch, T.G.
Welding Journal (Miami, Fla), 1974, 53 (07):
[28] The heat treatment features of welded joints of pipelines from corrosion-resistant steel
Korol'kov, P.M.
Svarochnoe Proizvodstvo, 2005, (07): : 48 - 52
[29] Influence of incomplete annealing of titanium (a + β)-alloy and its welded joints on fatigue resistance and corrosion-fatigue resistance
O. S. Kalakhan
V. I. Pokhmurs’kyi
Materials Science, 2000, 36 : 244 - 251
[30] Effect of hydrogen on reliability of high-strength corrosion-resistant steels
Kablov, E.N.
Krivonogov, G.S.
Metally, 2002, (01): : 42 - 51

← 1 2 3 4 5 →