Fracture behaviour of laminated veneer lumber under Mode I and III loading

被引：0

作者：

K. Frühmann

E. K. Tschegg

C. Dai

S. E. Stanzl-Tschegg

机构：

[1] Christian Doppler Laboratory for Fundamentals of Wood Machining at the Institute of Meteorology and Physics,

[2] University of Agricultural Sciences,undefined

[3] Türkenschanzstraße 18,undefined

[4] 1180 Vienna,undefined

[5] Austria e-mail: Klaus.fruchmann@ifp.tuwien.ac.at,undefined

[6] Intitute of Applied and Technical Physics,undefined

[7] Vienna University of Technology,undefined

[8] Wiedner Hauptstraße 8–10,undefined

[9] 1040 Vienna,undefined

[10] Austria,undefined

[11] Forintek Canada Corp,undefined

[12] 2665 East Mall,undefined

[13] Vancouver,undefined

[14] British Columbia,undefined

[15] Canada,undefined

[16] V6T 1W5,undefined

来源：

Wood Science and Technology | 2002年 / 36卷

关键词：

Crack Initiation; Fiber Orientation; State Crack; Laminate Veneer Lumber; Microstructural Damage;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Mode I and Mode III loading experiments were performed on side grooved CT specimens of two types of Laminated Veneer Lumber (LVL). Steady state crack propagation was maintained in order to detect complete load displacement diagrams. Fracture behaviour and influence of fiber orientation were studied and all important fracture mechanical values (stiffness/compliance, microstructural damage, crack initiation energy, specific fracture energy etc) were determined. Much higher crack initiation energies and specific fracture energies resulted in mode III loading than in mode I loading for both material types. Under external mode III loading, crack initiation occurs in mode III and crack propagation however takes place under mode I owing to crack surface interference. The influence of fiber orientation on fracture mechanical properties of LVL was discussed.

引用

页码：319 / 334

页数：15

共 50 条

[31] Potential fracture configurations of a cracked solid under mixed mode-I/III loading
Wang, L.
Xie, Y. J.
Yuan, H.
ARCHIVE OF APPLIED MECHANICS, 2023, 93 (05) : 2033 - 2049
[32] Potential fracture configurations of a cracked solid under mixed mode-I/III loading
L. Wang
Y. J. Xie
H. Yuan
Archive of Applied Mechanics, 2023, 93 : 2033 - 2049
[33] Effect of the loading rate on mode I interlaminar fracture toughness of laminated composites
Hug, G.
Thevenet, P.
Fitoussi, J.
Baptiste, D.
ENGINEERING FRACTURE MECHANICS, 2006, 73 (16) : 2456 - 2462
[34] Effect of Temperature on Fracture Toughness of Timetal 834 Titanium Alloy under Mode I and Mixed Mode I/III Loading
B.S.S. Chandra Rao
M. Srinivas
S.V. Kamat
Metallurgical and Materials Transactions A, 2008, 39 : 1340 - 1349
[35] Determination of coefficients of friction for laminated veneer lumber on steel under high pressure loads
Dorn, Michael
Habrova, Karolina
Koubek, Radek
Serrano, Erik
FRICTION, 2021, 9 (02) : 367 - 379
[36] Determination of coefficients of friction for laminated veneer lumber on steel under high pressure loads
Michael DORN
Karolína HABROVá
Radek KOUBEK
Erik SERRANO
Friction, 2021, 9 (02) : 367 - 379
[37] Determination of coefficients of friction for laminated veneer lumber on steel under high pressure loads
Michael Dorn
Karolína Habrová
Radek Koubek
Erik Serrano
Friction, 2021, 9 : 367 - 379
[38] Creep Behavior of Laminated Veneer Lumber from Poplar Under Cyclic Humidity Changes
Li, Chao
Huang, Yuxiang
BIORESOURCES, 2019, 14 (04) : 8018 - 8028
[39] Glulam Composed of Glued Laminated Veneer Lumber Made of Beech Wood: Superior Performance in Compression Loading
Dill-Langer, Gerhard
Aicher, Simon
MATERIALS AND JOINTS IN TIMBER STRUCTURES: RECENT DEVELOPMENTS OF TECHNOLOGY, 2014, 9 : 603 - 613
[40] Fractographic study of epoxy under mode I and mixed mode I/III loading
Ren, Fei
Wang, John Jy-An
Bertelsen, Williams D.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 532 : 449 - 455

← 1 2 3 4 5 →