Effect of ball scribing on relative permeability of grain-oriented electrical steel

Effect of ball scribing on relative permeability of conventional grain-oriented (CGO) and high permeability grain-oriented (HGO) electrical steel was investigated. The samples were scribed with spacing of 2 mm, 4 mm, 8 mm and 16 mm. The results show that after ball scribing with 16 mm width at 1.0 T, relative permeability of both CGO and HGO steels was increased by 109% and 80%, respectively. Relative permeability rises as the scribing space increases, with the movement of the peak value of relative permeability to a higher flux density. Relational models describing relative permeability and flux density were constructed with high accuracy based on experimental data. The experimental data curves were analyzed during the magnetizing process.